Abstract:Homogenously doped and mixed yttria stabilized zirconia, YSZ (with 3 and 10mol% Y2O3 known as 3YSZ and 10YSZ) and NiO/10YSZ co-precipitates (nominally corresponding to 7, 12, 24, 30, 35 and 45vol.% Ni metal), were synthesized using a continuous hydrothermal flow synthesis (CHFS) system which uses a stream of superheated water at 450°C and 24.1MPa as a reaction medium to cause rapid precipitation of metal oxide nanoparticle co-precipitates from a mixed metal salt solution. All products were obtained directly from the outlet of the CHFS reactor as a slurry, which was then cleaned and freeze-dried prior to further processing. The highly crystalline nano-powdered products were characterized using a range of analytical methods, including: powder X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), Raman spectroscopy and BET surface area measurements. Spherical primary particles of 10YSZ and 3YSZ were observed under the TEM and found to be 5.0±0.8nm (range 3.2–6.3nm) and 6.2±1.4nm (range 3.3–8.4nm) in size, with measured BET surface areas of 160.6 and 241.7m2g−1, respectively. Sintering of the nano-powder co-precipitates was performed via spark plasma sintering (SPS) at 1100°C for 1min, leading to densities of ca. 98% for 10YSZ and ca. 96% for Ni/10YSZ cermets (all NiO was converted into Ni due to the reducing atmosphere of the SPS). The 24% Ni/10YSZ cermet was subjected to focused ion beam tomography, which allowed the 3D arrangement of the conducting Ni metallic network of the dense cermet to be elucidated, and showed that a complete 3D network of Ni existed throughout the dense cermet disk. Electrical conductivity tests showed that the samples exhibited higher than expected electrical conductivity (for such low metal content), e.g., the 24vol.% Ni-containing sample achieved an electrical conductivity of ∼200Scm−1 at the fuel cell operating temperature, which corresponds to an effective conductivity of ∼117Scm−1 if a porosity of 30% were to be introduced.

Synthesis and Characteristics of La Doped Ceria–Zirconia Composite with Uniform Nano-Crystallite Dispersion

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Synthesis of Doped Ceria–zirconia Core–shell Nanocomposites Via Sol–gel Process

Highly conductive low nickel content nano-composite dense cermets from nano-powders made via a continuous hydrothermal synthesis route

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Mesoporous Yttria-Zirconia Solid Solution with Improved Textural Properties Prepared Via Lauric Acid-Assisted Synthesis

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Synthesis and microstructure of La-doped ceria nanoparticles.

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Dispersion behavior of zirconia nanocrystals and their surface functionalization with vinyl group-containing ligands.

Nano-dispersed yttria-stabilized zirconia powder: Phase, morphology, and conductivity investigation with different chelating agents via a modified sol-gel method

Fabrication, Microstructural Evolution, and Mechanical Properties of SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C Nanocomposites

Dispersion and Functionalization of Nonaqueous Synthesized Zirconia Nanocrystals Via Attachment of Silane Coupling Agents

Homogeneously Dispersed Ceria Nanocatalyst Stabilized with Ordered Mesoporous Alumina

Single-source-precursor synthesis of dense monolithic SiC/(Ti0.25Zr0.25Hf0.25Ta0.25)C ceramic nanocomposite with excellent high-temperature oxidation resistance

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

Preparation and Characterization of Ceria-Zirconia Ceramics Using a Sol-Gel Process

Mechanochemical dehydration and crystallization of supersaturated zirconia–alumina composite nano powders

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Synthesis of Nanostructured Nanoclay-Zirconia Multilayers: A Feasibility Study