Abstract:Pt/CeO2 catalysts with nanoporous structures were prepared by the facile dealloying of melt-spun Al92-XCe8PtX (X = 0.1; 0.3 and 0.5) ribbons followed by calcination. The phase compositions and structural parameters of the catalysts were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and high-resolution transmission electron microscopy (HRTEM). The specific surface area and pore size distribution were characterized by N-2 adsorption-desorption tests. The catalytic properties were evaluated by a three-way catalyst (TWC) measurement system. The results revealed that the dealloyed samples exhibited a nanorod framework structure. The Pt nanoparticles that formed in situ were supported and highly dispersed on the CeO2 nanorod surface and had sizes in the range of 2-5 nm. For the catalyst prepared from the melt-spun Al91.7Ce8Pt0.3 ribbons, the 50% CO conversion temperature (T-50) was 91 degrees C, and total CO could be converted when the temperature was increased to 113 degrees C. An X-ray photoelectron spectroscopy (XPS) test showed that the Pt-0.3/CeO2 sample had a slightly richer oxygen vacancy; and a H-2 temperature-programmed reduction (H-2-TPR) test demonstrated its superior adsorption ability for reduction gas and high content of active oxygen species. The experiments indicated that the catalytic performance could be retained without any attenuation after 130 h when water and CO2 were present in the reaction gas. The favorable catalytic activities were attributed to the high specific areas and small pore and Pt particle sizes as well as the strong interactions between the CeO2 and Pt nanoparticles. The Pt nanoparticles were embedded in the surface of the CeO2 nanorods, inhibiting growth. Therefore, the catalytic stability and water resistance were excellent.

Homogeneously Dispersed Ceria Nanocatalyst Stabilized with Ordered Mesoporous Alumina

In-situ Formed Stable Pt Nanoclusters on Ceria-Zirconia Solid Solutions Induced by Hydrothermal Aging for Efficient Low-Temperature CO Oxidation

A facile route to ordered mesoporous-alumina-supported catalysts, and their catalytic activities for CO oxidation.

Embedding Ultrafine and High-Content Pt Nanoparticles at Ceria Surface for Enhanced Thermal Stability.

Facile Alcohothermal Synthesis, Size-Dependent Ultraviolet Absorption, and Enhanced CO Conversion Activity of Ceria Nanocrystals

Crystal Facet Induced Single-Atom Pd/CoxOyon a Tunable Metal-Support Interface for Low Temperature Catalytic Oxidation

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Facile Route for Synthesizing Ordered Mesoporous Ni–Ce–Al Oxide Materials and Their Catalytic Performance for Methane Dry Reforming to Hydrogen and Syngas

Thermally Stable Pt/CeO(2) Hetero-Nanocomposites with High Catalytic Activity.

Surfactant-Mediated One-Pot Method to Prepare Pd–CeO2 Colloidal Assembled Spheres and Their Enhanced Catalytic Performance for CO Oxidation

Stabilization of Exposed Metal Nanocrystals in High‐Temperature Heterogeneous Catalysis

Controlled Synthesis of Sintering-Resistant Pd@CeO2 Core–Shell Nanotube Catalysts for CO Oxidation

Facile Synthesis of Highly Dispersed and Well‐Alloyed Bimetallic Nanoparticles on Oxide Support

Ultrafine platinum/iron oxide nanoconjugates confined in silica nanoshells for highly durable catalytic oxidation

Synthesis of Cerium-Oxide Coated Platinum Core-Shell Structure Catalysts with Enhanced Stability and Activity Via Atomic Layer Deposition

Structure-activity relationship of Pt catalyst on engineered ceria-alumina support for CO oxidation

Ultrastable PtCo/Co3O4-SiO2 Nanocomposite with Active Lattice Oxygen for Superior Catalytic Activity Toward CO Oxidation.

The Preparation And Catalytic Properties Of Nanoporous Pt/Ceo2 Composites With Nanorod Framework Structures

Textural, Structural, and Morphological Characterizations and Catalytic Activity of Nanosized CeO2–MOx (M = Mg2+, Al3+, Si4+) Mixed Oxides for CO Oxidation

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties