Abstract:The effect of coating cracking during depth-sensing indentation testing (e.g. nanoindentation testing) on systems comprising thin hard coatings (e.g. TiN) on a less stiff, hard substrate (e.g. steel) has been investigated in order to establish whether, at such small scales, the occurrence of annular through-thickness cracks around indentation sites can be detected from load–displacement plots and whether any accompanying localized debonding of the coating from the substrate can also be identified. Experiments were performed on thin TiN and NbN monolayers, and compositionally modulated TiN/NbN and TiN/ZrN deposited onto hard steel or stainless steel substrates. Above a critical load (Pcrit) in the range 80–500mN, all systems exhibited annular through-thickness cracks around indentation sites. The cracking was found to be accompanied by a discrete change in gradient of the loading portion of the load–displacement curve. Also, analysis of the unloading curves beyond this point showed that elastic recovery was controlled by the elastic modulus of the underlying substrate material alone. The cracking mechanism has been characterized using scanning electron microscopy, coupled with optical profilometry to map the detailed z-displacement of the surface — a procedure critical to understanding whether coating–substrate debonding had occurred. Some cracks were found to show a spiral morphology and the effect of indentation loading rate was investigated to see if appearance of these cracks was loading-rate sensitive. Our results highlight the problems inherent in assessing both the interfacial failure and the interfacial fracture toughness of thin film coated systems at the small contact scales (⩽1μm) associated with crack genesis where it is difficult to confirm the extent of sub-surface cracks by conventional means. We have also demonstrated that both load–displacement and load–displacement squared plots are necessary if a more complete understanding of system behaviour is to be gained. Also, a simple fracture mechanics model for the annular cracking behaviour seen in such systems has been derived and used to estimate a value of Gic (the interfacial work of fracture) as 180Jm−2 for the TiN/ZrN-stainless steel system.

The Nanoindentation-Induced Cracking of Thin Silicon Chips

Atomistic Investigations of Single-Crystal Silicon with Pre-Existing Defects

Mechanism of crack evolution in nano-indentation of single crystal silicon by atomistic simulations and theoretical analysis

Depth-sensing ductile and brittle deformation in 3C-SiC under Berkovich nanoindentation

Multiscale Simulation of Surface Defects Influence Nanoindentation by a Quasi-Continuum Method

Fracture Toughness Evaluation and Plastic Behavior Law of a Single Crystal Silicon Carbide by Nanoindentation

Strength/Crack-Size Relationship for Knoop-Indented Bending Specimens and Its Application to Silicon Nitride Ceramics

The effect of coating cracking on the indentation response of thin hard-coated systems

A Study on the Collapse of Self-Similar Hardening Behavior of Nanostructures

Multiscale Analysis of Size Effect of Surface Pit Defect in Nanoindentation

Multiscale simulation and Rice-Thomson dislocation model analysis of nanoindentation

Micro/nanoscale mechanical characterization and in situ observation of cracking of laminated Si3N4/BN composites

Intensified chipping during nanoindentation and the effect of friction on the interfacial fracture for thin films used in N/MEMS

Microscopic Model for Fracture of Crystalline Si Nanopillars During Lithiation

On the Fracture Toughness Measurement of Thin Film Coated Silicon Wafers

Nanomechanics and Nanocomposites: Mechanical Behaviors

Modelling Nano-Indentation of Ion-Irradiated FCC Single Crystals by Strain-Gradient Crystal Plasticity Theory

Simulation Of Near-Crack-Tip Strain Fields On Single-Crystal Silicon Wafer

Size Dependent Morphologies of Brittle Silicon Nitride Thin Films with Combined Buckling and Cracking

Cracking in semiconductor devices–effect of plasticity under triaxial constraint

Indentation of Coatings at micro/nano scale: Crack formation and deflection