Microwave dielectric properties of Li3A3Te2O12 (A = Y, Yb) garnets for low temperature cofired ceramic technologies
Ying Tang,Huan Li,Jie Li,Huaicheng Xiang,Liang Fang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.12.079
IF: 5.7
2022-05-01
Journal of the European Ceramic Society
Abstract:Te6+-containing microwave dielectric ceramics Li3A3Te2O12 (A = Y, Yb) with low firing temperatures were prepared using the solid-state reaction method. Li3Y3Te2O12 and Li3Yb3Te2O12 can be obtained as garnet single-phase ceramics with low sintering temperatures of 940 ℃ and 950 ℃, respectively. The cations, such as Li+, Te6+, and Y3+/Yb3+, fully occupied the tetrahedral, octahedral, and dodecahedral sites of garnet structure, respectively. Li3A3Te2O12 (A = Y, Yb) ceramics exhibit εr ∼ 7.83 ± 0.2 and 5.94 ± 0.2, Q × f ∼ 47,800 ± 500 GHz and 41,800 ± 500 GHz, and τf ∼ –47 ± 3.0 ppm/°C and –76 ± 3.0 ppm/°C, respectively. The full width at half-maximum (FWHM) values of the A1g Raman mode correlate negatively with the Q × f values. Moreover, Li3A3Te2O12(A = Y, Yb) ceramics possess good chemical compatibility with the Ag electrode, making them promising candidates for low-temperature cofired ceramics (LTCC) technologies.
materials science, ceramics