Influence on Microstructure and Magnetic Performance of Co-doped Mg Ferrites by Low Temperature Sintering
Gaojie Zou,Gongwen Gan,Liwen Dian,Yue Cheng,Yaqin Yin,Jie Luo,Chenhao Zhang,Guoqing Gou,Fei Xie
DOI: https://doi.org/10.1007/s11665-024-10413-w
IF: 2.3
2024-12-11
Journal of Materials Engineering and Performance
Abstract:This work investigated the effect of Co 2+ ions substitution on microstructure and magnetic properties of Mg 1−x Co x Fe 2 O 4 (x = 0.0, 0.2, 0.4, 0.6, and 0.8) bulk ferrites, which was successfully synthesized by low temperature (960 °C) with 5 wt.% Bi 2 O 3 . XRD analysis confirmed that the samples have spinel cubic space group and lattice parameter increase linearly with Co 2+ content. The SEM results indicate that the grains of samples are highly agglomerated relatively uniform from 2 to 2.3 μm. Meanwhile, the experimental density (ρ E ) of samples increases from 4.35 to 4.65 g/cm 3 with the increase of Co 2+ content and relative density (ρ R ) of all samples reach 90%. VSM test results demonstrate that the saturation magnetization ( Ms ) increases from 25 to 68 emu/g, and the value of coercivity ( Hc ) increases from 3 to 373 Oe. This work provides a reference for ferrite sintered by low temperature solid-state method, making the preparation process more low-carbon and environmentally friendly.
materials science, multidisciplinary