Abstract:Abstract This paper presents an experimental study of Cu-Mo alloys prepared by powder metallurgy (PM) method. Also, improving the dispersion and wettability of Mo in the Cu matrix was aimed. Mo particles were added by 0.24, 0.48, 0.73 and 0.97% volume fraction to Cu powder. The mixture was mechanically milled by planetary ball mill at a rotational speed of 140 rpm for 24 h under hydrogen atmosphere, with milling ball size of ∼25 times the size of the metal powders. Liquid acetone was utilized as a process control agent (PCA). Paraffin wax (0.5 wt%) was used to decrease the friction with die during the compaction process. The mixture of the blended powder was compacted at ambient temperature under three different pressures (400, 600 and 800 MPa) and then sintered in a vacuum furnace at 1000 °C for 1 h by a heating rate of 5 °C min −1 . The microstructure examination showed a homogeneous dispersion of Mo particles within the Cu matrix with no evidence of new phases formation during the sintering process. Also, the relative density of samples has been increased by increasing both of Mo content and the compaction pressure. The results revealed that the compaction pressure of 600 MPa was the most suitable pressure as it gave the highest densification. Cu—0.97% volume fraction Mo alloy samples exhibited finer Mo particles with a homogenous distribution in the Cu matrix and well bonding with the Cu particles. The microhardness was increased gradually by increasing Mo wt%, while the compressive strength was decreased by increasing the Mo contents. Both the electrical and thermal conductivities were decreased gradually by the addition of Mo. While the coefficient of thermal expansion (CTE) was decreased by Mo addition.

Sintering Behavior of Mo/Cu Composite Powders Prepared by Electroless Copper Plating on Molybdenum Powders

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Sintering Behavior of W–30Cu Composite Powder Prepared by Electroless Plating

Enhancing the physical properties of Mo-Cu composites through plasma spheroidized spherical molybdenum powder

Achieving Homogeneous Fe Distribution and High Strength in Cu-Fe Composite Consolidated by Powder Rolling

Effects of Simplified Pretreatment Process on the Morphology of W–Cu Composite Powder Prepared by Electroless Plating and Its Sintering Characterization

The Influence of Ball Milling Conditions on the Powder Characteristics and Sintering Densification of Mo-Cu Alloy

Preparation and Properties of W-15Cu Composite by Electroless Plating and Powder Metallurgy

Densification and Properties Investigation of W-Mo-Cu Composites Prepared by Large Current Electric Field Sintering with Different Technologic Parameter

Influences of Metal Oxide Additions on the Morphology of Sintered AgSnO2 Composite Powders

Study of Hot-press Sintering Process of Nanometer Cu-Al_2O_3 Composite

Influences of Tin Oxide Surface Modification on the Morphology and Performance of Sintered Ag/SnO2 Composite Powders

Influence of impurities on the sintering densification in nano- Al2O3 powders coated by copper

Improving the mechanical properties and coefficient of thermal expansion of molybdenum-reinforced copper using powder metallurgy

Formation Mechanism of W-coated Cu Composite Powders and the Metal Injection Molding Using Polyoxymethylene-Based Binders

Preparation and properties of W-Mo-Cu composite using solution combustion synthesized W Mo solid solution nanopowder

Enhanced softening resistance and mechanical properties of Mo 2 C particle-reinforced Cu-matrix composites

Effects of Sintering Method on Density and Microstructure of Particulate Reinforced Copper Matrix Composites

Fabrication and microstructure of W-Cu composites prepared from Ag-coated Cu powders by electroless plating

Preparation and properties of lead-free copper matrix composites by electroless plating and mechanical alloying

Fabrication of W–Cu/La2O3 Composite Powder with a Novel Pretreatment Prepared by Electroless Plating and Its Sintering Characterization