Abstract:Novel Ni-doped TaN (Ni-Ta-N) films are deposited by remote plasma-enhanced atomic layer deposition (ALD) with pentakis(dimethylamino) tantalum, nickelocene, and NH3 precursors for Cu diffusion barriers. Various Ni-Ta-N films with different compositions are achieved by changing the deposition cycles (n) of Ni sublayer while fixing the deposition cycles of TaN sublayer at 2. As n increases from 1 to 6, the root-mean-square roughness of the deposited film increases from 0.150 to 0.527 nm, and the resistivity decreases from 0.18 to 1.1 x 10(-2) Omega cm. After annealing at 400 degrees C for 30 min in the forming gas (N-2/H-2), these films still maintain an amorphous texture and demonstrate a negligible reduction of resistivity and a weak increase of density. Subsequently, the barrier effects of the Ni-Ta-N films with different compositions are compared against Cu diffusion after annealing. The results reveal that the Ni-Ta-N films with n <= 4 exhibit barrier effects comparable with the ALD TaN film even after annealing at 550 degrees C. Further, a 3 nm ultrathin Ni-Ta-N film with n = 4, corresponding to an addition of similar to 22 at. % Ni to TaN, cannot only reduce the film resistivity by 78% but also effectively block Cu diffusion after annealing at 450 degrees C for 30 min. Published by the AVS.

High-quality Ru thin film grown on TaN by plasma enhanced atomic layer deposition(PEALD)

Ru thin film grown on TaN by plasma enhanced atomic layer deposition

Comparison of the Ru thin films grown on Si, TiN/Si and TaN/Si substrates by plasma enhanced atomic layer deposition

ALD Growth of Ru on RIE-pretreated TaN Substrate

Effect of Pretreatment of TaN Substrates on Atomic Layer Deposition Growth of Ru Thin Films

The physical properties of cubic plasma-enhanced atomic layer deposition TaN films

Ru Thin Film Formation Using Oxygen Plasma Enhanced ALD and Rapid Thermal Processing

Ruthenium Barrier/Seed Layer for Cu/Low-κ Metallization

Investigation of Ru/TaN on low dielectric constant material with k=2.7

Ca2RuO4 Thin Film Growth by Pulsed Laser Deposition

Hydrogen Plasma-Assisted Atomic Layer Deposition of Ru with Low Oxygen Content

Growth of cubic-TaN thin films by plasma-enhanced atomic layer deposition

TiN/AlN Nano Multilayers Film Fabricated by Plasma Enhanced Atomic Layer Deposition

Diffusion Barrier Properties of TaNx Films Prepared by Plasma Enhanced Atomic Layer Deposition from PDMAT with N2 or NH3 Plasma

Improved Barrier Properties of Ultrathin Ru Film with Tan Interlayer for Copper Metallization

Deposition of TiN and TaN by Remote Plasma ALD for Cu and Li Diffusion Barrier Applications

Atomic layer deposition of amorphous Ni-Ta-N films for Cu diffusion barrier

The properties of Ru on Ta-based barriers

Thermal Stability of Ultrathin RuC Film As Cu Diffusion Barrier

Sputtered Ru–Ti, Ru–N and Ru–Ti–N Films As Cu Diffusion Barrier

Growth Of Ruo2 Thin Layer On Ru(1010) Studied By Scanning Tunneling Microscopy