Abstract:The native oxide layer that forms on copper (Cu) metal spherical particle surfaces under ambient handling conditions has been shown to have a significant effect on sintering behavior during microwave heating in a previous study, where an abnormal expansion was observed and characterized during sintering of Cu compacts using reducing gases. Because microwave (MW) heating is selective and depends greatly on the dielectric properties of the materials, this thin oxide layer will absorb MW energy easily and can consequently be heated drastically starting from room temperature until the reduction process occurs. In the current study, this oxide ceramic layer was qualitatively and quantitatively characterized using the carrier gas hot extraction (CGHE) method, Auger electron spectroscopy (AES), and a dual-beam focused ion beam (FIB)/scanning electron microscope (SEM) system that combines both FIB and SEM in one single instrument. Two different commercial gas-atomized spherical Cu metal powders with different particle sizes were investigated, where the average oxygen content of the powders was found to be around 0.575 wt% using the CGHE technique. Furthermore, AES spectra along with depth profile measurements were used to qualitatively characterize this oxide layer, with only a rough quantitative thickness approximation due to method limitations and the electron beam reduction effect. For the dual-beam FIB-SEM system, a platinum (Pt) coating was first deposited on the Cu particle surfaces prior to any characterization in order to protect and to preserve the oxide layer from any possible beam-induced reduction. Subsequently, the Pt-coated Cu particles were then cross-sectioned in the middle in situ using an FIB beam, where SEM micrographs of the resulted fresh sections were characterized at a 36° angle stage tilt with four different detector modes. Quantitative thickness characterization of this native oxide layer was successfully achieved using the adapted dual-beam FIB-SEM setup with more accuracy. Overall, the native Cu oxide layer was found to be inhomogeneous over the particles, and its thickness was strongly dependent on particle size. The thickness ranged from around 22-67 nm for Cu powder with a 10 µm average particle size (APS) and around 850-1050 nm for one with less than 149 µm.

Preparation and characterization of porous copper powder by thermal decomp osition of complicated copper oxalate

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

Preparation and Characterization of Talc/Nano-Cu Conductive Composite Powder

A Facile Template-Free Preparation of Porous Manganese Oxides by Thermal Decomposition Method

Preparation And Characterization Of One-Dimensional Porous Zinc Oxide Constructed By Nanocrystal

A Catalytic Oxidation Approach to Coat Copper Powder with Polyaniline

Synthesis of Porous Manganese Oxides Bars Via A Hydrothermal-Decomposition Method

OXIDATION BEHAVIOR OF FINE COPPER POWDER IN AIR BETWEEN 250-400 ℃

Preparation and Characterization of Copper Oxide Nanoparticles Through Solid State Thermal Decomposition of an Aqua Nitrato Copper(II) Complex with a Tridentate Schiff-base Ligand as a New Precursor

Preparation Mechanism and Catalytic Performance of Porous Copper-Doped Calcium Phosphate Material

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Hydrothermal Preparation of CuAlO2 Powder

Preparation, characterization and catalytic property of CuO nano/microspheres via thermal decomposition of cathode-plasma generating Cu2(OH)3NO3 nano/microspheres.

Influence of impurities on the sintering densification in nano- Al2O3 powders coated by copper

Preparation and characterization of hierarchical nanostructures composed by CuO nanowires within directional microporous Cu

Chemical Synthesis, Characterization and Thermal Analysis of Polyaniline/Copper Composite Powder

Rapid preparation of micro/nano porous Cu/Cu 2 O particles through dealloying of powder sintered Cu-Al alloy

Characterization of the Native Oxide Shell of Copper Metal Powder Spherical Particles

Preparation method of ultra-low-oxygen spherical micron copper powder

In-situ Synthesis and Characterization of Three-dimensional Porous Micro-nano Structured Copper Azide

The Preparation of an Ultrafine Copper Powder by the Hydrogen Reduction of an Ultrafine Copper Oxide Powder and Reduction Kinetics