Abstract:Influence of the pouring temperature ranging from 680 to 780 °C on the solidification behavior, the microstructure and mechanical properties of the sand-cast Mg−10Gd−3Y−0.4Zr alloy was investigated. It was found that the nucleation undercooling of the α-Mg phase increased from 2.3 to 6.3 °C. The average α-Mg grain size increased from 44 to 71 μm, but then decreased to 46 μm. The morphology of the eutectic compound transformed from a continuous network into a discontinuous state and then subsequently into an island-like block. The volume fraction of β-Mg24RE5 phase increased and its morphology transformed from particle into rod-like. The increase in pouring temperature increased the solute concentration. YS increased from 138 to 151 MPa, and UTS increased from 186 to 197 MPa. The alloy poured at 750 °C had optimal combining strength and ductility. The fracture surface mode transformed from quasi-cleavage crack into transgranular fracture, all plus the dimple-like fracture, with the micro-porosity and the re-oxidation inclusion as major defects. The average α-Mg grain size played a main role in the YS of sand-cast Mg−10Gd−3Y−0.4Zr alloy, besides other factors, i.e. micro-porosity, morphology of eutectic compounds, re-oxidation inclusion and solute concentration.

Microstructures and morphology evolution of icosahedral phase of as-cast Mg67.4Zn28.9Y3.7 ternary alloy subjected to the pouring temperature

Growth and morphology evolution of icosahedral quasicrystal phase in Mg 30Zn 60Y 10 alloy

Growth and Morphology Evolution of Icosahedral Quasicrystal Phase in Mg_(30)Zn_(60)Y_(10) Alloy

Growth morphology and evolution of icosahedral quasicrystal in Mg-Zn-Y ternary alloys

Solidification of Mg-28%Zn-2%Y Alloy Involving Icosahedral Quasicrystal Phase

Microstructure and phase transformation of as-cast and annealed Mg–4Zn–1Y alloy containing quasi-crystal phase

Effect of Zn and Y on microstructures and properties of normally-solidified Mg-Zn-Y alloys

Solidification of Mg28zn2y and Icosahedral Quasicrystal Morphology Evolution

Formation and Growth of Icosahedral Quasicrystal in Mg30Zn60Y10 Alloy

Study on Solidification Process, Microstructures and the Primary Phase of Peritectic Reaction of Mg70zn28y2 Alloy

Growth Morphology and Evolution of Quasicrystal in As-Solidified Y-Rich Mg-Zn-Y Ternary Alloys

Morphologies of Quasicrystal Phase in Ternary Mg-Zn-Y Alloys

Influence of pouring temperature on solidification behavior, microstructure and mechanical properties of sand-cast Mg-10Gd-3Y-0.4Zr alloy

Icosahedral quasicrystal structure of the Mg40Zn55Nd5 phase and its thermodynamic stability

Microstructure evolution of Mg-10Gd-3Y-1.2Zn-0.4Zr alloy during heat-treatment at 773 K

Microstructure and Phase Transformation of Forged Mg–3.7Zn–0.3Y–0.3Gd Quasicrystal Alloy

Effect of Icosahedral Quasicrystalline Fraction and Extrusion Ratio on Microstructure, Mechanical Properties, and Anisotropy of Mg-Zn-Gd-Based Alloys

Effects of extrusion on the microstructure and mechanical properties of Mg–Zn–Gd alloy reinforced with quasicrystalline particles

Stable Icosahedral Phase in Mg–Zn–Gd Alloy

Effects of Cooling Rate on Morphology, Microhardness and Volume Fraction of Mg-Zn-Y Quasicrystals

Microstructure characterization on Mg-2Nd-4Zn-1Zr alloy during heat treatment