Abstract:The CuAlO2 films were prepared on glass and quartz substrates by radio frequency magnetron sputtering with a sintered target composed of Al(OH)3 and Cu2O powders. X-ray diffraction analyses reveal that the as-deposited films are amorphous structure and the as-annealed films are predominated by the CuAlO2 phase along with the Al2O3 phase. Scanning electron microscope (SEM) measurements indicate that grains grow up and surface becomes rougher as a result of increasing temperature. The optical studies show that annealing leads to the reduction of the average transmittance of the films from 60% to 40% for the visible range and the decrease of the fitted refractive index from 2.0 to 1.5. Direct band gaps confirmed by the transmittance and reflectance measurements are estimated to be 3.86 and 3.50 eV for as-deposited and as-annealed films, respectively. As increasing exposure time, water contact angles of the as-deposited films exposed under ultraviolet light source 365 nm or 254 nm decrease from 96.3° and 96.4° to 87.5° and 87.2°, respectively. The variation of contact angle can be attributed to the hydrophobic organic stains on the surface, surface roughness, the formation of Cu2+, and band gap variation of CuAlO2 film. The as-annealed film becomes hydrophilic and its water contact angle is 31.1°. The wetting property of CuAlO2 films is very important for the wide spread application of this material.

Microstructure and Optical Properties of Agxo Prepared by Direct-Current Magnetron-Sputtering Method

Microstructure and Optical Properties of Ag-MgO Composite Cluster Films

Microstructure and Optical Properties of ZnO Films Deposited by Radio-frequency Reactive Magnetron Sputtering

Ellipsometric Study of the Optical Properties of Silver Oxide Prepared by Reactive Magnetron Sputtering

Deposition and Characterization of AZO Thin Films on Flexible Glass Substrates Using DC Magnetron Sputtering Technique

Study of Structure and Optical Properties of Silver Oxide Films by Ellipsometry, XRD and XPS Methods

Influence of O_2/Ar Flow Ratio on Microstructures and Photoluminescence of ZnO Films

Modulation of Optical and Electrical Properties of Sputtering-Derived Amorphous Ingazno Thin Films by Oxygen Partial Pressure

Room temperature deposited silver oxide films by dc magnetron sputtering with high sputtering power: effect of deposition time on microstructure, electrical and optical properties

Optical and Wetting Properties of CuAlO2 Films Prepared by Radio Frequency Magnetron Sputtering

Sol-Gel Preparation of Ag/ZnO Films and Their Electrical and Optical Properties

Preparation and Properties Investigation of AgOx Mask Films

The effects of oxygen flow ratio on the properties of Ag x O thin films grown by radio frequency magnetron sputtering

La0.67(Ca0.24Sr0.09)MnO3:xAg2O (0 ≤ X ≤ 0.25) Composites with Improved Room–temperature TCR and MR for Advanced Uncooling Infrared Bolometers and Magnetic Sensors

Preparation and Microstructures of CoAg Granular Films with Giant Magnetoresistance

Characterization of AZO and Ag based films prepared by RF magnetron sputtering

Optical properties of aluminum silver alloy films deposited by magnetron sputtering

Ag/PEO Nanocomposite Fabricated in a Planar Magnetron Sputtering

Structural, Electrical And Optical Properties Of Zn1-Xmgxo Films Prepared By Reactive Dc Sputtering

Initial Growth and Oxygen Adsorption of Silver on Al2O3 Film

Optical and electronic properties of (Al Ga1−)2O3/Al2O3 (x>0.4) films grown by magnetron sputtering