Effect of Multi-Stage Ageing Treatments on Microstructures and Mechanical Properties of New-Type Al-Cu-Li Alloy

LI Hong-ying,ZHANG Xiao-jun,ZHANG Jian-fei,ZHENG Zi-qiao

DOI: https://doi.org/10.3321/j.issn:1004-0609.2008.03.009

2008-01-01

The Chinese Journal of Nonferrous Metals

Abstract:The effects of multi-stage ageing treatments on the microstructures and mechanical properties of Al-Cu-Li alloys were investigated. The results show that, the alloys with higher mechanical properties by two-stage and three-stage ageing treatments can be obtained. When the alloy is aged at higher temperature(165 ℃), δ′, θ′, T1 and σ phases are precipitated, and the fine and dispersed phases are precipitated at 130 ℃, which improves the strength of alloy. The GP zones or transition phases are preferentially precipitated when the alloy is pre-aged at 150℃, and many second-phases are precipitated at 165 ℃, the fine phases are precipitated under the third stage treatments, which results in higher combined strength properties.