Abstract:Co-evaporation of Cu-KF-In-Se was performed on substrates with varied Na supply. Compositions of interest for photovoltaic absorbers were studied, with ratios of (K + Cu)/In ∼ 0.85 and K/(K + Cu) ∼ 0–0.57. Bare soda-lime glass (SLG) substrates had the highest Na supply as measured by secondary ion mass spectrometry, while SLG/Mo and SLG/SiO2/Mo substrates led to 3x and 3000x less Na in the growing film, respectively. Increased Na supply favored Cu1−xKxInSe2 (CKIS) alloy formation as proven by X-ray diffraction (XRD), while decreased Na supply favored the formation of CuInSe2 + KInSe2 mixed-phase films. Scanning electron microscopy and energy dispersive X-ray spectroscopy revealed the KInSe2 precipitates to be readily recognizable planar crystals. Extrinsic KF addition during film growth promoted diffusion of Na out from the various substrates and into the growing film, in agreement with previous reports. Time-resolved photoluminescence showed enhanced minority carrier lifetimes for films with moderate K compositions (0.04 < K/(K + Cu) < 0.14) grown on SLG/Mo. Due to the relatively high detection limit of KInSe2 by XRD and the low magnitude of chalcopyrite lattice shift for CKIS alloys with these compositions, it is unclear if the lifetime gains were associated with CKIS alloying, minor KInSe2 content, or both. The identified Na-K interdependency can be used to engineer alkali metal bonding in Cu(In,Ga)(Se,S)2 absorbers to optimize both initial and long-term photovoltaic power generation.

The Influence of Na on Elements Diffusion of Cu(In,Ga)Se2 Thin Films

Effects Of Na Incorporated At Different Periods Of Deposition On Cu(In, Ga)Se-2 Films

Increasing surface band gap of Cu(In,Ga)Se2 thin films by post depositing an In-Ga-Se thin layer.

Influences of Na on Sintering of Cu(In, Ga)Se-2 Quaternary Ceramic Targets

Influence of Ga Concent of CuInGa Precursor on Stoichiometry of Cu(In1 - xGax) Se2 Photon Absorption Films

Investigation of Cu(In,Ga)Se2 Polycrystalline Growth: Ga Diffusion and Surface Morphology Evolution

The effect of Na on Cu-K-In-Se thin film growth

Gallium Diffusion in Cigs Thin Films Prepared by Sequential Sputtering/Selenization Technique

Na Incorporation in Cu(In,Ga)(Se,S) 2 Films Grown on Insulator-Coated Stainless Steel Foil Using a Metal Precursor Reaction

Research progress on synthesis of CuIn 1-xGa xSe 2 nanoparticles

Effects of Alkali Elements on Copper Indium Gallium Aluminum Selenide Flexible Solar Cells Fabricated on Polyimide Substrates

The Optical Influence of Na on Cu 2 ZnSnSe 4 Films Deposited with Na-containing Sol–gel Precursor

Influence of Carrier Gas on Microstructures and Morphologies of Cu(In_(1-x)Ga_x)Se_2 Films

The Role of Na Incorporation in the Low-Temperature Processed CIGS Thin Film Solar Cells Using Post Deposition Treatment

Preparation And Characterization Of Cu(In,Ga)Se-2 Thin Films By Selenization Of Cu0.8ga0.2 And In2se3 Precursor Films

Effects of Sb-doping on the grain growth of Cu(In, Ga)Se2 thin films fabricated by means of single-target sputtering

The Influence of Indium Surfactant on the Electrical Properties of GaN Epilayers Grown by Metal-Organic Chemical Vapour Deposition

Na‐Diffusion Enhanced p‐type Conductivity in Cu(In,Ga)Se2: A New Mechanism for Efficient Doping in Semiconductors

Research progress on synthesis of CuIn1-x Gax Se2 nanoparticles

Influence of Bilayer Precursor Films on Structure and Morphology of CIGS Films

Influence of Lamination Modes of CuInGa Precursor Films on Composition and Microstructures of Selenized CuInGa Absorber