Ultrasonic-assisted in situ synthesis and characterization of superparamagnetic Fe 3O 4 nanoparticles
Jie Feng,Jian Mao,Xiaogang Wen,Mingjing Tu
DOI: https://doi.org/10.1016/j.jallcom.2011.06.053
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Superparamagnetic Fe 3O 4 nanoparticles were synthesized via a modified coprecipitation method, and were characterized with X-ray diffraction (XRD), vibrating sample magnetometer (VSM), Zeta potential and FT-IR, respectively. The influences of different kinds of surfactants (sodium dodecyl benzene sulfonate, polyethyleneglycol, oleic acid and dextran), temperatures and pH values on the grain size and properties were also investigated. In this method, Fe 3+ was used as the only Fe source and partially reduced to Fe 2+ by the reducing agent with precise content. The following reaction between Fe 3+, Fe 2+ and hydroxide radical brought pure Fe 3O 4 nanoparticles. The tiny fresh nanoparticles were coated in situ with surfactant under the action of sonication. Comparing with uncoated sample, the mean grain size and saturation magnetization of coated Fe 3O 4 nanoparticles decrease from 18.4 nm to 5.9-9.0 nm, and from 63.89 emu g -1 to 52-58 emu g -1 respectively. When oleic was used as the surfactant, the mean grain size of Fe 3O 4 nanoparticles firstly decreases with the increase of reaction temperature, but when the temperature is exceed to 80 °C, the continuous increase of temperature resulted in larger nanoparticles. the grain size decreases gradually with the increasing of pH values, and it remains unchanged when the PH value is up to 11. The saturation magnetization of as-prepared Fe 3O 4 nanoparticles always decreases with the fall of grain size. © 2011 Elsevier B.V. All rights reserved.