1D Magnetic Materials of Fe 3 O 4 and Fe with High Performance of Microwave Absorption Fabricated by Electrospinning Method

Rui Han,Wei Li,Weiwei Pan,Minggang Zhu,Dong Zhou,Fa-shen Li

DOI: https://doi.org/10.1038/srep07493

IF: 4.6

2014-01-01

Scientific Reports

Abstract:Fe 3 O 4 and Fe nanowires are successfully fabricated by electrospinning method and reduction process. Wiry microstructures were achieved with the phase transformation from α-Fe 2 O 3 to Fe 3 O 4 and Fe by partial and full reduction, while still preserving the wire morphology. The diameters of the Fe 3 O 4 and Fe nanowires are approximately 50–60 nm and 30–40 nm, respectively. The investigation of microwave absorption reveals that the Fe 3 O 4 nanowires exhibit excellent microwave absorbing properties. For paraffin-based composite containing 50% weight concentration of Fe 3 O 4 nanowires, the minimum reflection loss reaches −17.2 dB at 6.2 GHz with the matching thickness of 5.5 mm. Furthermore, the calculation shows that the modulus of the ratio between the complex permittivity and permeability |ε/μ| is far away from unity at the minimum reflection loss point, which is quite different from the traditional opinions.