Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Solution Synthesis and Novel Magnetic Properties of Ball-Chain Iron Nanofibers

1D Magnetic Materials of Fe 3 O 4 and Fe with High Performance of Microwave Absorption Fabricated by Electrospinning Method

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Electrospinning Of Fe, Co, And Ni Nanofibers: Synthesis, Assembly, And Magnetic Properties

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Synthesis and characterization of novel magnetic Fe3O4/polyphosphazene nanofibers

Synthesis And Microwave Absorption Properties Of Fe@Carbon Fibers

Synthesis and Magnetic Studies of Fe–Ni Nanofibres by Electrospinning

Nanoscale Characterization and Magnetic Reversal Mechanism Investigation of Electrospun NiFe2O4 Multi-Particle-chain Nanofibres.

Thermomechanical properties of confined magnetic nanoparticles in electrospun polyacrylonitrile nanofiber matrix exposed to a magnetic environment: Structure, Morphology, and Stabilization (Cyclization)

Fabrication and Magnetic Properties of Electrospun Fe2NiGa Nanofibers

Structure and Magnetic Properties of Electrospun Co0.6Ni0.3Zn0.1Fe2O4 and Co0.6Ni0.3Cu0.1Fe2O4 Nanofibers

Improved Ferromagnetic Properties of Electrospun NiFe2O4 with Tunable Morphology: from Multiparticle-Chain to Single-Particle-chain

High-Strength Single-Walled Carbon Nanotube/Permalloy Nanoparticle/Poly(vinyl alcohol) Multifunctional Nanocomposite Fiber.

Microwave Absorption Properties of Amorphous Iron Nanostructures Fabricated by a High-Yield Method

Fabrication, characterization, exchange coupling and magnetic behavior of CoFe2O4/CoFe2 nanocomposite nanofibers

A Novel Carbon Nanotubes/fe3o4 Inorganic Hybrid Material: Synthesis, Characterization and Microwave Electromagnetic Properties

Electrospun magnetic carbon composite fibers: Synthesis and electromagnetic wave absorption characteristics

Electromagnetic Properties and Microwave Absorption of Electrospun Fe2O3-Carbon Composite Nanofibers with Particle–Nanorod Structure

Electrospinning Fabrication, Characterization and Magnetic Properties of Co0.5Ni0.5Fe2O4 Nanofibers

About Some Resonance, Structural, and Magnetic Properties of Amorphous and Nanocrystalline FeCuNbSiB Ribbons