Structure and Magnetic Properties of Electrospun Co0.6Ni0.3Zn0.1Fe2O4 and Co0.6Ni0.3Cu0.1Fe2O4 Nanofibers

Jianfeng DAI,Xiguang TIAN,Xingshan YAN,Weixue LI,Qing WANG

DOI: https://doi.org/10.11896/j.issn.1005-023X.2017.022.007

2017-01-01

Abstract:In this paper ,the precursor of Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4/PVP and Co0 .6 Ni0 .3 Zn0 .1 Fe2 O4/PVP nanofibers with uniform diameter and smooth surface were prepared by electrospinning technique .Then the Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4/PVP and Co0 .6 Ni0 .3 Zn0 .1-Fe2 O4/PVP nanofibers were obtained via heat treatment at 500—900 ℃ .The phase ,morphology ,structure and magnetic properties of the resultant Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4 and Co0 .6 Ni0 .3 Zn0 .1 Fe2 O4 nanofibers were characterized by TG-DSC ,XRD ,SEM and VSM respectively .The results show that the pure phase and well crystallized Co0.6Ni0.3Cu0.1Fe2O4 and Co0.6Ni0.3Zn0.1Fe2O4nanofibers or staple fibers can be obtained after heat treatment in the air by heat treatment at 500—900 ℃ .When the temperature is at 700 ℃ ,the diameter of Co0.6 Ni0.3 Cu0.1 Fe2O4 and Co0.6 Ni0.3 Zn0.1 Fe2O4 nanofibers with smooth surface is about 80 nm ,and moreover ,the Co0.6Ni0.3Cu0.1Fe2O4 nanofibers retain a high remanence ratio (Mr/Ms) and a coercivity of 0 .56 and 1088 .87 Oe respectively .At 500 ℃ ,600 ℃ ,700 ℃ ,800 ℃ ,900 ℃ ,Co0 .6 Ni0 .3 Zn0 .1 Fe2 O4 nanofibers exhibit the intensities of saturation magnetization which are 14 .5% ,7% ,16% ,10 .7% ,8% higher than those of Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4 nanofibers respectively ,as well as the coercive forces which are 38% ,51% ,50% ,46% ,46 .7% lower than Co0 .6 Ni0 .3 Cu0 .1 Fe2 O4 nanofibers respectively .The differences of saturation magnetization and coercivity of the two nanofibers provide a good reference for electromagnetic applications of CoNi ferrite .