Effect of Calcination Temperature on Microstructure and Magnetic Properties of Ni0.3cu0.2zn0.5fe2o4 Nanofibers

Xiang Jun,Shen Xiangqian,Chu Yanqiu,Zhou Guangzhen,Guo Yintao

2010-01-01

Acta Chimica Sinica

Abstract:The Ni0.3Cu0.2Zn0.5Fe2O4 nanofibers with diameters of around 100 nm were successfully fabricated by sol-gel method combined with electrospinning technology. The as-spun polymer/inorganic composite nanofibers and calcined products were characterized by means of thermogravimetric and differential thermal analysis (TG-DTA), X-ray powder diffraction (XRD), fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The experimental results showed that the pure spinet structure was basically formed when the composite nanofibers were calcined at 450 degrees C for 2 h. With the increase of calcination temperature, the nanofiber surface became much rougher and the nanofiber morphology gradually changed toward the necklace-like structure along with the growth of Ni0.3Cu0.2Zn0.5Fe2O4 grains contained in the nanofibers. At the same time, the specific saturation magnetization (M-s) of nanofibers monotonously increased, while the coercivity (H-c) initially increased, reached a maximum value at about 650 degrees C, and then decreased with further increasing calcination temperature, indicating that the single-domain critical size of Ni0.3Cu0.2Zn0.5Fe2O4 in the form of nanofibers may be around 53 nm. Furthermore, the relationship between the coercivity of Ni0.3Cu0.2Zn0.5Fe2O4 nanofibers and the mean grain size (D) was analyzed in a D range below the single-domain critical size. It was found that H-c of these nanofibers varied as D-0.71, which was in good agreement with the predicted D-2/3 dependence of H-c on the basis of the random anisotropy model.