Abstract:Fe3O4 magnetic nanoparticles with mean diameter of about 6 nm coated by PEG4000 were prepared by a precipitation method with ferric chloride and ferrous sulfate as starting materials and ammonia for alkalinizing,and the Fe3O4-PEG4000 magnetic nanoparticles obtained were further modified by citric acid through ultrasonic treatment.Afterwards,NH2 end group surface functionalized Fe3O4 magnetic nanoparticles Fe3O4@SiO2-NH2were prepared through Stober method using silane coupling agent.Further,positively charged ionic polyurethane(IPU) was grafted onto the surface of Fe3O4@SiO2 nanoparticles by polymerization of NH2 end group,presynthesized ionic diol,PEG200 and toluylene-2,4-diisocyanate(TDI).Finally,Fe3O4/CdTe/polyurethane(Fe3O4/CdTe/IPU) nanocomposites were prepared by electrostatic interaction of positively charged IPU and thioglycolic acid coated CdTe quantum dots(QDs).The structure of Fe3O4/CdTe/IPU nanocomposites was characterized and verified by XRD,FTIR,TGA,TEM,VSM,UV and PL analyses.It was found through XRD spectra that Fe3O4/CdTe/IPU nanocomposites were a mixture of cubic-structural Fe3O4 nanoparticles,amorphous SiO2 and cubic-structural CdTe QDs.According to the FTIR analyses,the chemical bonds of SiO2,IPU and Fe3O4 indicated that SiO2 and IPU were grafted onto the surface of Fe3O4 nanoparticles.The results of TGA indicated that the coating amount of IPU was about 40%(W/W).TEM analyses showed that the SiO2 coated Fe3O4 nanoparticles were well dispersed which had a relatively uniform diameter of about 20 nm,and the CdTe QDs were arranged around the magnetic nanoparticles.The hysteresis loops proved the superparamagnetic properties of the as-prepared magnetic nanoparticles and nanocomposites.The UV and PL spectra suggested the nanocomposites revealed the properties of the QDs,and the UV irradiation images showed that the QDs moved and aggregated with magnetic nanoparticles in the magnetic field.

Synthesis and Magnetic Properties of PEG-Modified Fe3O4 Nanospheres

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

A Facile Synthesis of Superparamagnetic Hybrid Hollow Nanospheres Based on Monodisperse Nickel–zinc Ferrite/polyethylene Glycol and Their Electromagnetic, Microwave Absorbing Properties

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Ph Responsive Behavior of Fe3O4@PDEA-PEGMA Core-Shell Hybrid Magnetic Nanoparticles

Synthesis of N-Hexadecylphosphonic Acid-Coated Monodisperse Fe3O4 Superparamagnetic Nanoparticles

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Magnetron Sputtering Synthesis Silver and Organic PEO Nanocomposite

Facile Synthesis of Size-Controllable Monodispersed Ferrite Nanospheres

Adsorption Properties of Fe_3O_4/Poly(acrylate-methyl-ester) Magnetic Microspheres for Metal Ions

Synthesis Of Fe3O4 nanoparticles of iron sand coprecipitation methodwith polyethylene glycol 6000

Synthesis and characterization of PEG coated hollow Fe3O4 magnetic nanoparticles as a drug carrier

Synthesis, Surface Modification and Characterization of Magnetic Fe3O4@SiO2 Core-Shell Nanoparticles

PREPARATION OF Fe_3O_4/CdTe/POLYURETHANE NANOCOMPOSITES AND THEIR PROPERTIES

Preparation and Characterization of Ferromagnetic Fluids Modified by Carboxyl PEG

Research on Modification of Fe3O4 Magnetic Nanoparticles with Two Silane Coupling Agents

Effective PEGylation of Fe<SUB>3</SUB>O<SUB>4</SUB> Nanomicelles for <i>in Vivo</I> MR Imaging

Preparation of Monodispersed Hybrid Nanospheres with High Magnetite Content from Uniform Fe3O4 Clusters

Preparation and Surface Modification of Fe<sub>3</sub>O<sub>4 &Lt;/sub>nano-Magnetic Powders