Abstract:Fe-Si-Al-Cr ∞aky particles were used as microwave absorbing material. Iron-Silicon- Aluminum-Chromium ingots with nominal compositions Fe73Si15Al10Cr2 were produced by al- loying the pure elements in an induction melting furnace under argon atmosphere at 0.03MPa, and then the ingots were crushed into irregular shaped particles. As-crushed alloy had been milled by planetary miller for 32h. In order to increase the efiective permeability, the material was annealed under difierent conditions. The morphology of the powders was characterized by scanning electron microscope (SEM). The phases of powders were estimated by X-ray difiract ometer (XRD). The microwave permeability dispersion spectra of annealed powders within a frequency range of 0.5{8GHz was measured. The SEM results showed that particles had been successfully transformed into the ∞aky shape. The average diameter of ∞akes is about 43"m. The average aspect ratio (width/thickness) of ∞akes is about 28. The XRD results showed that the DO3 ordered phase coexisted with fi-Fe(Si,Al,Cr) matrix phase by annealing above 500 - C. When the annealing temperature increased from room temperature to 800 - C, the grain size grown from 10.4nm to its maximum 29.8nm and part of fi-Fe(Si,Al,Cr) matrix phase translated into DO3. The imaginary part of the efiective permeability increased with the annealing temperature, and decreased when the temperature was above 500 - C. The resonance frequency decreased with the annealing temperature, and increased when the temperature was above 400 - C. The efiec- tive permeability of the powders, obtained by 500 - C annealing, had a maximum value of 6.0 at 2.5GHz.

Microwave Absorbing Capability of FeSi Nano-crystalline Flakes

Microwave absorbing capability of nanocrystalline flakes

Microwave absorbing capability of Fe85Si1Al6Cr8 nanocrystalline flakes

Microstructure and Electromagnetic Properties of Fe-Si-Al Flakes Produced from Melt-Spun Ribbons

Microwave absorbing mechanism of soft magnetic alloy Fe85Si2Al6Cr7

Electromagnetic and Microwave Absorption Properties of Surface Modified Fe–Si–Al Flakes with Nylon

Superior Microwave Absorption Properties of Carbon-Coated FeSiCr Micro Flakes

Microwave Absorption Properties of Fesi Flaky Particles Prepared Via A Ball-Milling Process

Synthesis Method and Absorption Application of Nanocrystalline Alloy Flakes

Effect of heat treatment on the microwave electromagnetic properties of flaky Fe-Si-Al magnetic powders

Enhance the Magnetic Properties of Fe-Si-Al-Cr Flaky Particles by Annealing

Electromagnetic and microwave absorbing properties of the composites containing flaky FeSiAl powders mixed with MnO 2 in 1–18GHz

Microwave electromagnetic properties of FeNi alloy particles composites doping with FeCuNbSiB nanocrystalline microwires

Synthesis of Hexagonal Fe Microflakes with Excellent Microwave Absorption Performance

Percolation and Microwave Characteristics of CoFeB–SiO2 Nano-Granular Films

Grain size modulation to optimize the wave-absorbing properties of FeSiCr alloy micropower

Effects of particle morphology and crystal structure on the microwave properties of flake-like nanocrystalline Fe3Co2 particles

Nanocrystalline structure and particle size effect on microwave permeability of FeNi powders prepared by mechanical alloying

A study of electromagnetic characteristics of Fe-Si-Al magnetic alloy

Enhancing the Microwave Absorption Properties of Fe-Cu-Nb-Si-B Nanocomposite Flakes by Coating with Spinel Ferrite NiFe2O4

Flaky FeSi particles with tunable size, morphology and microstructure developing for high-efficiency and broadband absorbing materials