Lithium Ion Intercalation-Induced Metal-Insulator Transition in Inclined-Standing Grown 2D Non-Layered Cr2S3 Nanosheets
Wanghua Hu,Jinbo Shen,Tao Wang,Zishun Li,Zhuokai Xu,Zhefeng Lou,Haoyu Qi,Junjie Yan,Jialu Wang,Tian Le,Xiaorui Zheng,Yunhao Lu,Xiao Lin
DOI: https://doi.org/10.1002/smtd.202400312
IF: 12.4
2024-01-01
Small Methods
Abstract:Gate-controlled ionic intercalation in the van der Waals gap of 2D layered materials can induce novel phases and unlock new properties. However, this strategy is often unsuitable for densely packed 2D non-layered materials. The non-layered rhombohedral Cr2S3 is an intrinsic heterodimensional superlattice with alternating layers of 2D CrS2 and 0D Cr1/3. Here an innovative chemical vapor deposition method is reported, utilizing strategically modified metal precursors to initiate entirely new seed layers, yields ultrathin inclined-standing grown 2D Cr2S3 nanosheets with edge instead of face contact with substrate surfaces, enabling rapid all-dry transfer to other substrates while ensuring high crystal quality. The unconventional ordered vacancy channels within the 0D Cr1/3 layers, as revealed by cross-sectional scanning transmission electron microscope, permitting the insertion of Li+ ions. An unprecedented metal-insulator transition, with a resistance modulation of up to six orders of magnitude at 300 K, is observed in Cr2S3-based ionic field-effect transistors. Theoretical calculations corroborate the metallization induced by Li-ion intercalation. This work sheds light on the understanding of growth mechanism, structure-property correlation and highlights the diverse potential applications of 2D non-layered Cr2S3 superlattice.