Abstract:Stacks of a few intrinsic tunnel junctions were micro-fabricated on the surface of Bi-2212 single crystals. The number of junctions in a stack was tailored by progressively increasing the height of the stack by ion-beam etching, while its tunneling characteristics were measured in-situ in a vacuum chamber for temperatures down to ~13 K. Using this in-situ etching/measurements technique in a single piece of crystal, we systematically excluded any spurious effects arising from variations in the junction parameters and made clear analysis on the following properties of the surface and inner conducting planes. First, the tunneling resistance and the current-voltage curves are scaled by the surface junction resistance. Second, we confirm that the reduction in both the gap and the superconducting transition temperature of the surface conducting plane in contact with a normal metal is not caused by the variation in the doping level, but is caused by the proximity contact. Finally, the main feature of a junction is not affected by the presence of other junctions in a stack in a low bias region.

Stacks of Intrinsic Josephson Junctions Singled out from Inside Bi2sr2cacu2o8+X Single Crystals

Fabrication Of Stacked Intrinsic Josephson Junctions From Bi2sr2cacu2o8+X Thin Films

Intrinsic Josephson Junctions: Integrated Circuits and Possible Applications

Three-dimensional array of intrinsic Josephson junctions in Bi2Sr2CaCu2O8+x single crystals

Microwave Responses of an Insular Intrinsic Josephson Junction Stack Fabricated from Bi-Sr-Ca-Cu-O Single Crystal

Acid Etching Process for Fabrication of Bi2sr2cacu2o8-X Stack

Exploring the Versatility of Double-Sided Fabrication of Intrinsic Josephson Junctions

Intrinsic Josephson Junction Arrays Containing Only a Few Junctions

Progressive evolution of tunneling characteristics of in-situ fabricated intrinsic Josephson junctions in Bi_2Sr_2CaCu_2O_{8+delta} single crystals

Three-Dimensional Arrays of Bisrcacuo-2212 Intrinsic Josephson Junctions and Zero-Crossing Shapiro Steps at 760 Ghz

Individual Shapiro Steps Observed In Resistively Shunted Intrinsic Josephson Junctions On Bi2sr2cacu2o8+X Single Crystals

Fabrication and Characteristics of Intrinsic Josephson Junctions in Bi 2 Sr 2 CaCu 2 O 8+x Single Crystals

Terahertz Applications of Integrated Circuits Based on Intrinsic Josephson Junctions in High Tc Superconductors

Bi2sr2cacu2o8 Intrinsic Josephson Junction Stacks With Improved Cooling: Coherent Emission Above 1 Thz

Double-Side Fabrication Process and Millimeter Wave Response of Intrinsic Josephson Junctions

Thermal and Electromagnetic Properties of Bi2sr2cacu2o8 Intrinsic Josephson Junction Stacks Studied Via One-Dimensional Coupled Sine-Gordon Equations

Fluxons in Long and Annular Intrinsic Josephson Junction Stacks

Intrinsic Josephson Junctions in Bisrcacuo-2212: Recent Progress

<title>Terahertz applications of integrated circuits based on intrinsic Josephson junctions in high Tc superconductors</title>

Terahertz Emission from Bi 2 Sr 2 CaCu 2 O 8 + Δ Intrinsic Josephson Junction Stacks with All-Superconducting Electrodes

Bi2sr2cacu2o8+Delta Intrinsic Josephson Junctions Fabricated By A Simple Technique Without Photolithography