Abstract:In the present study, titanium carbide powders with suitable morphology and nanometer particle size were synthesized by the sol-gel method to investigate the parameters affecting the properties of sol and the final powder. The initial sol was prepared in a four-component system of alkoxide-water-alcohol-citric acid based on the chemical process of sol-gel. study of sol properties showed that pH was the most important factor in the control of sol conditions and particle size so that at low pHs, due to low concentration of OH- ions and reduced viscosity, it was easier to control the particles size. Accordingly, the results of the Dynamics Light Scattering (DLS) showed that at low pHs, the particles size was below 10 nm. According to the zeta potential diagram and by examining the conditions of sol at different pHs, 4.5 was determined as the optimal pH and to prevent the bonding of particles within the sol, ammonium polycarboxylate dispersant was used. The temperature at which particles were formed was determined using Differential thermal analysis (DTA) and Thermal gravimetric analysis (TG). X-ray diffraction (XRD) patterns showed the presence of a completely amorphous phase at 700 ̊C. It was also observed that with increasing temperature, TiC crystallization started from 1200 ̊C and ended at 1400 ̊C. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) micrographs at 1400 ̊C showed the completely spherical morphology of particles of nanometer size so that no agglomerate was observed.

Synthesizing nano-scale titanium nitride powders by solvothermal and carbothermal methods

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Preparation of nano-TiN powders by Ni-catalysed carbothermal reduction nitridation

Synthesis of Ti(C,N) ultrafine powders by carbothermal reduction of TiO2 derived from sol–gel process

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Preparation of TiN ultrafine powders from sol-gel by Fe-catalyzed carbothermal reduction nitridation

Exploring the impact of pH and temperature on TiC nanopowders syntesized via sol-gel and subsequent crystallization by carbothermal reduction method

The synthesis of nanosized TiO2 powder using a sol-gel method with TiCl4 as a precursor

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

Synthesis of Nanocrystalline Titanium Nitride Powders by Direct Nitridation of Titanium Oxide

Synthesis of Nanosized Titanium‐Chromium Oxynitride Powders by Ammonolysis of Coprecipitated TiO2/Cr2O3 Precursors

Carbothermal Preparation of Ultra-Fine TiB2 Powders Using Solution-Derived Precursors Via Sol-Gel Method

Synthesis of titanium dioxide nano-powder via sol–gel method at ambient temperature

Sintering of nanocrystalline titania

Nano Β-Sialon Powder Synthesized by Carbothermal Reduction and Nitridation of Ultrafine Al2O3-SiO2 Mixture Employing Sol-Gel Techniques

Synthesis of Nanopowders of Titanium Nitride by In-Situ Nitridation of Titanium Oxide

Controlling crystallinity of nano-titania powder prepared by the hydrolysis of titanium alkoxide

Synthesis of ZnTiO3 Ceramic Powders by Sol-Gel Method

Low-Temperature Synthesis of Titanium Oxynitride Nanoparticles