Abstract:To get the best metallic phase composition and learn the distribution of impurities in the melts during electrolysis, NiFe2O4-NiO based cermet inert anodes with different type of metallic phases were prepared, the solubility test was conducted in a cryolite based melt, and the corrosion resistance and impurities distribution during electrolysis were tested. Results showed that, the solubility values of NiFe2O4-NiO based cermets with different metallic phases in the cryolite based melt can not be used to effectively differentiate their corrosion resistance. In the electrolysis tests, the steady-state concentrations of impurity Ni were close to its solubility, but the steady-state concentrations of impurity Fe and Cu were far lower than its solubility; the average values of total impurity concentrations for cermets 17Cu/ (NiFe2O4-NiO), 17Ni/ (NiFe2O4-NiO) and 17(85Cu-15Ni)/ (NiFe2O4-NiO), were 307ppm, 304ppm and 373ppm respectively. It had not been concluded decidedly that the metal Cu had more potential than Ni as metallic phase for the NiFe2O4-NiO based cermets inert anodes in aluminium electrolysis. The impurities Ni and Fe are unevenly distributed with a concentration gradient between the anodic area and cathodic area after the corrosion of Ni-NiFe2O4-NiO cermet anodes during electrolysis happened.

Effect of Cu content on the corrosion behaviour of Cu/(10NiO-90NiFe 2O4) cermets in aluminum electrolysis

Effect of cu content on the corrosion behaviour of Cu/(10NiO-9ONiFe(2)O(4)) cermets in aluminum electrolysis

Influence of Ni Addition on Corrosion Performance of Medium-temperature Filler Metal with Low Cu Content for Al Brazed Joints

Effect of Ni Content on Corrosion Behavior of Ni/(10nio-90nife(2)O(4)) Cermet Inert Anode

On the corrosion behaviour of NiFe2O4-NiO based cermets as inert anodes in aluminum electrolysis

Effect of Metallic Phase Species on the Corrosion Resistance of 17M/(10nio-Nife2o4) Cermet Inert Anode of Aluminum Electrolysis

Anodic Corrosion Behavior of NiFe 2 O 4 -Based Cermet in Na 3 AlF 6 -K 3 AlF 6 -AlF 3 for Aluminum Electrolysis

Effect of Electrolysis Superheat Degree on Anticorrosion Performance of 5Cu/(10nio-Nife2o4) Cermet Inert Anode

Electrical Conductivity of Cu/（10NiO-NiFe 2 O 4 ） Cermet Inert Anode for Aluminum Electrolysis

Effect of Additive BaO on Corrosion Resistance of Xcu/(10nio-Nife2o4) Cermet Inert Anodes for Aluminum Electrolysis

Anodic Corrosion Behavior of NiFe2O4-Based Cermet in Na3AlF6-K3AlF6-AlF3 for Aluminum Electrolysis

On the Corrosion Behaviour of Ni-Nio-Nife(2)O(4) Cermets As Inert Anodes in Aluminum Electrolysis

Effect of NiO Content on Corrosion Behaviour of Ni-xNiO-NiFe2O4 Cermets in Na3AlF6-Al2O3 Melts

Effect of Metallic Content on Properties of NiFe2O4 Matrix Cermet Inert Anodes for Aluminum Electrolysis

Materials Fabrication and Corrosion Behavior of NiFe2O4 Cermet Inert Anodes

Effect of coated spinel NiFe_2O_4 in the surface of metal phase 20Ni-80Cu on corrosion resistance of 15(20Ni-80Cu)/85(NiFe_2O_4-10NiO) cermet for aluminum electrolysis

Effect of metallic content on sintering behavior of NiFe2O4-based cermet inert anode for aluminum electrolysis

Effect of Operating Parameters on Corrosion Behavior of NiFe2O4 Cermet Inert Anodes

Effect of coated spinel NiFe204 in the surface of metal phase 20Ni-80Cu on corrosion resistance of 15（20Ni-80Cu）/85（NiFe20~-10NiO） cermet for aluminum electrolysis

Effect of Sintering Atmosphere on Corrosion Resistance of Ni/(NiFe2O4–10NiO) Cermet Inert Anode for Aluminum Electrolysis

Preparation of a cermet inert anode based on ferrous nickel and its use in an electrolysis study