Abstract:Low-k SiONC thin films with excellent thermal stabilities were deposited using plasma-assisted molecular layer deposition (PA-MLD) with a tetraisocyanatesilane (Si(NCO)4) precursor, N2plasma, and phloroglucinol (C6H3(OH)3). By adjusting the order of the N2plasma exposure steps within the PA-MLD process, we successfully developed a deposition technique that allows accurate control of thickness at the Ångström level via self-limiting reactions. The thicknesses of the thin films were measured through spectroscopic ellipsometry (SE). By tuning the N2plasma power, we facilitated the formation of -NH2sites for phloroglucinol adsorption, achieving a growth per cycle of 0.18 Å cycle-1with 300 W of N2plasma power. Consequently, the thickness of the films increased linearly with each additional cycle. Moreover, the organic linkers within the film formed stable bonds through surface reactions, resulting in a negligible decrease in thickness of approximately -11% even upon exposure to a high annealing temperature of 600 °C. This observation was confirmed by SE, distinguishing the as-prepared film from previously reported low-k films that fail to maintain their thickness under similar conditions. X-ray photoelectron spectroscopy (XPS) and current-voltage (I-V) and capacitance-voltage (C-V) measurement were conducted to evaluate the composition, insulating properties, and dielectric constant according to the deposition and annealing conditions. XPS results revealed that as the plasma power increased from 200 to 300 W, the C/Si ratio increased from 0.37 to 0.67, decreasing the dielectric constant from 3.46 to 3.12. Furthermore, there was no significant difference in the composition before and after annealing, and the hysteresis decreased from 0.58 to 0.19 V owing to defect healing, while maintaining the leakage current density, breakdown field, and dielectric constant. The low dielectric constant, accurate thickness control, and excellent thermal stability of this MLD SiONC thin film enable its application as an interlayer dielectric in back-end-of-line process.

Low Residual Stress and High Repeatability of SiNX Thin Films for InP-based Optoelectronic Device Fabrication by Dual Radio Frequency Plasma Enhanced Chemical Vapor Deposition

Preparation Of Low-K Nanoporous Sio2 Films By Plasma-Enhanced Chemical Vapor Deposition

Deposition of Dense SiO2 Thin Films for Electrical Insulation Applications by Microwave ECR Plasma Source Enhanced RF Reactive Magnetron Sputtering

Floating Low-Temperature Radio-Frequency Plasma Oxidation of Polycrystalline Silicon-Germanium

PROPERTIES OF PECVD SiNx FILM FOR SOLAR CELLS

Remote Plasma Atomic Layer Deposition of SiNx Using Cyclosilazane and H2/N2 Plasma

Stability of SiNx Prepared by Plasma-Enhanced Chemical Vapor Deposition at Low Temperature

Room-temperature deposition of low H-content SiNx/SiNxOy thin films using a specially designed PECVD system

Room Temperature Dry Etching of INP-Based Semiconductors for Optoelectronic Device Fabrication Using Inductively Coupled Plasma

Low-Temperature Deposition of High-Quality SiO2 Films with a Sloped Sidewall Profile for Vertical Step Coverage

Study of SiO2 Films Prepared by Electron Cyclotron Resonant Microwave Plasma

Synthesis of low-k SiONC thin films by plasma-assisted molecular layer deposition with tetraisocyanatesilane and phloroglucinol

A Comparison of Structures and Properties of SiNx and SiOx Films Prepared by PECVD

Low-temperature deposition of high-quality silicon oxynitride films for CMOS-integrated optics

Stressor SiNx contact etch stop layer (CESL) technology and its application in nano-scale transistors

Impact of H-Related Chemical Bonds on Physical Properties of SiNx:H Films Deposited via Plasma-Enhanced Chemical Vapor Deposition

Optimization of Fabrication Process for SiON/SiOx Films Applicable as Optical Waveguides

Optimization of PECVD silicon oxynitride films for anti-reflection coating

Fabrication of High Quality Patterned Soi Materials by Optimized Low-Dose Simox

Enhanced photonics devices based on low temperature plasma-deposited dichlorosilane-based ultra-silicon-rich nitride (Si8N)

Plasma-enhanced atomic layer deposition of silicon nitride thin films with different substrate biasing using Diiodosilane precursor