Abstract:Based on principles of chemical thermodynamics, the relationship between temperature and the Gibbs free energy of erosion products generated during the sulfate attack on cement concrete was deduced. The orientation of chemical reactions of sulfate attack on cement concrete was theoretically determined as well as the critical sulfate ion concentration and the formation conditions of erosion products. The phase composition, microstructure, crystal form, and morphology of erosion products before and after sulfate attack were investigated by environmental scanning electron microscope and energy spectrum analysis (ESEM-EDS) and X-ray diffraction (XRD). The results show that the effects of sulfate ion concentration and temperature on cement concrete sulfate attack are significant, and different influencing factors correlate with each other. The crystal transition temperature between the anhydrite and dihydrate gypsum is 42°C, and the corresponding concentration of sulfate ion is about 2.3 × 10 −3 mol/L. Simultaneously, the crystal transition temperature between the thenardite and mirabilite is 32.4°C. Moreover, the theoretical upper limit temperature and sulfate ion lower limit concentration of thaumasite are 44°C and 0.0023 mol/L, respectively. The ESEM-EDS and XRD results imply that the chemical thermodynamics can be used to reveal the erosion mechanism of sulfate attack on cement concrete. The major erosion products of sulfate attack on cement concrete are rod-like ettringite with a larger slenderness ratio, plate-like gypsum, granular sulfate salt, incompletely corroded calcium hydroxide, and residual skeleton of calcium silicate hydrate. The sulfate attack has double effects on mechanical properties of specimens, which can affect the microstructure, phase composition, type, and morphology of erosion products.

INFLUENCE OF ENVIRONMENTAL CHARACTERISTICS ON SULFATE ATTACK TYPES OF CEMENT MORTARS

Thaumasite form of sulfate attack in limestone cement concrete: The effect of cement composition, sand type and exposure temperature

Attack of Limestone Cement-Based Material Exposed to Magnesium Sulfate Solution at Low Temperature

Thaumasite form of sulfate attack in ettringite rich-ternary systems: Effects of limestone filler, etching solutions and exposure temperature

Thermodynamic investigation of the formation mechanism of thaumasite in cement-ground limestone cementitious materials under sulfate attack

Impact of the Thaumasite Sulfate Attack on the Pore Structure and Gas Permeability of Cement Mortar

Form and mechanism of sulfate attack on cement-based material made of limestone powder at low water-binder ratio under low temperature conditions

Contradict mechanism of long-term magnesium and sodium sulfate attacks of nano silica-modified cement mortars – Experimental and thermodynamic modeling

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Research on Sulfate Attack Mechanism of Cement Concrete Based on Chemical Thermodynamics

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Influence of Ca2+ on Early Degradation of Cast-In-Situ Mortar Induced by Sulfate-Magnesium Multiple Combined Attack

Analysis of Sulfate Substance Penetration into the Surface Area of Hardened Cement Mortar and Its Reaction Products

Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Chemical–physical–mechanical Stability of MKG Mortars under Sulfate Attacks

RESEARCH ON MECHANISM OF SULFATE ATTACK ON CONCRETE BY TG-DSC METHOD

Effect of Different Mineral Admixtures on Sulfate Attack to Mortars

Experimental and theoretical investigation on hydraulic fracturing in cement mortar exposed to sulfate attack

Effect of Exposure Conditions on Mortar Subjected to an External Sulfate Attack

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution