Abstract:Based on principles of chemical thermodynamics, the relationship between temperature and the Gibbs free energy of erosion products generated during the sulfate attack on cement concrete was deduced. The orientation of chemical reactions of sulfate attack on cement concrete was theoretically determined as well as the critical sulfate ion concentration and the formation conditions of erosion products. The phase composition, microstructure, crystal form, and morphology of erosion products before and after sulfate attack were investigated by environmental scanning electron microscope and energy spectrum analysis (ESEM-EDS) and X-ray diffraction (XRD). The results show that the effects of sulfate ion concentration and temperature on cement concrete sulfate attack are significant, and different influencing factors correlate with each other. The crystal transition temperature between the anhydrite and dihydrate gypsum is 42°C, and the corresponding concentration of sulfate ion is about 2.3 × 10 −3 mol/L. Simultaneously, the crystal transition temperature between the thenardite and mirabilite is 32.4°C. Moreover, the theoretical upper limit temperature and sulfate ion lower limit concentration of thaumasite are 44°C and 0.0023 mol/L, respectively. The ESEM-EDS and XRD results imply that the chemical thermodynamics can be used to reveal the erosion mechanism of sulfate attack on cement concrete. The major erosion products of sulfate attack on cement concrete are rod-like ettringite with a larger slenderness ratio, plate-like gypsum, granular sulfate salt, incompletely corroded calcium hydroxide, and residual skeleton of calcium silicate hydrate. The sulfate attack has double effects on mechanical properties of specimens, which can affect the microstructure, phase composition, type, and morphology of erosion products.

Analysis of Sulfate Substance Penetration into the Surface Area of Hardened Cement Mortar and Its Reaction Products

Diffusion Characteristic of Sulfate Anion in Surface Region of Cement Mortar at Early Stage

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Form and mechanism of sulfate attack on cement-based material made of limestone powder at low water-binder ratio under low temperature conditions

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Effect of Exposure Conditions on Mortar Subjected to an External Sulfate Attack

Impact of Leaching and Chlorides on Sulfate Attack for Cement Paste

Influence of Super Absorbent Polymer on the Sulfate Resistance of Cement Mortar

Research on Sulfate Attack Mechanism of Cement Concrete Based on Chemical Thermodynamics

Influence of the Initial Moist Curing Time on the Sulfate Attack Resistance of Concretes with Different Binders

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Relationship Between Microscopic Pore Structure and Strength of Cement-Based Materials with Low Water-Binder Ratio Under Sulfate Attack Environment

Sulfate resistance and hydration products of steam cured steel slag blended cement mortar under dry–wet cycle

Effect of ultrafine slag powder addition on performance of cement mortar subjected to ( NH4) 2SO4 solution

Deterioration of Mortar Bars Using Binary and Ternary Mixtures Immersed in Sodium Sulfate Solutions

Research on the Sulfate-resistant Chemical Attack Mechanism of Concrete with Mineral Admixture

Influence of internal sulfate attack on cement paste properties: contamination by pyrite

Ultrasonic and impact spectroscopy monitoring on internal sulphate attack of cement-based materials