Ti-based Nano-diamond Coating Field Emission Cathode

Chun-xue ZHAI,Zhi-yong ZHANG,Xue-wen WANG,Wu Zhao,Jun-feng YAN
2007-01-01
Abstract:A new type of field emission cathode was devised. Nano-diamond powders were coated on the surface of titanium by spinning coating. After thermal treatment under proper condition in vacuum system, the bonding between diamond and substrate could be realized, and the cathode was formed with titanium as substrate, TiC as interlayer and nano-diamond powders as emitters. This kind of field emission cathode is adapted to large area preparation and batch production. The lowest threshold electric field of the samples as-prepared can be 6.3 V/μm, and the current density can reach to 60.7 μA/cm2 at the field of 21 V/μm. The structure model of samples was supposed and the electron transmission mode during emission process was analyzed. According to conventional field emission theory, the emitted electrons mainly follow the field emission mechanism because of their approximately straight Fowler-Nordheim(F-N) plots. Before gained the stable field emission state, the excited process was observed and this phenomenon was explained.
What problem does this paper attempt to address?