Abstract:In terms of the mechanisms of methanol synthesis from synthesis gas and methanol dehydration, it was predicted that the yield of dimethyl ether (DME) would be greatly increased if the inter-dispersion of the oxide particles in the catalyst was enhanced. For comparison, 4 methods-- bi-hydrolysis precipitation and three other methods were used to prepare the catalysts: (1) Low-dispersion mixing: A commercial Cu/Zn/Al methanol catalyst having a size range of 20--40 mesh was mechanically mixed with a dehydration catalyst {gamma}-alumina with the same size range; (2) High-dispersion mixing: The two catalysts used in 1 were ground together to {minus}200 mesh and pelletized and then crushed to 20--40 mesh; (3) Co-precipitation impregnation as reported in a cited reference; (4) Bi-hydrolysis precipitation: An aqueous solution of mixed nitrates of copper and zinc and an aqueous solution of NaAlO{sub 2} were simultaneously dropped into a beaker containing some deionized water. A precipitate was formed which was filtered, washed, dried and calcined. The particle size of the catalysts prepared by methods 3 and 4 charged into the reactor were in the same range as those by methods 1 and 2. Catalysts prepared by methods 1, 2, 3 and 4 are designated as Cat-1, Cat-2, Cat-3more » and Cat-4 respectively. The inter-dispersion of the oxides particles were in the order of Cat-1 < Cat-2 < Cat-3 < Cat-4. The catalysts were evaluated for activity in a tubular flow reactor with a feed having a mole composition of H{sub 2}/CO/CO{sub 2} = 64/31/5 under 270 C, 3 MPa and a space velocity of 2000 h{sup {minus}1}. Results are presented in a table and briefly discussed.« less

Effect of the Content of Metallic Component on Cu-Mn-Zn/Y Catalysts for Direct Synthesis of DME

Effect of copper content on Cu–Mn–Zn/zeolite-Y catalysts for the synthesis of dimethyl ether from syngas

A NOVEL PREPARETION OF Cu-Mn CATALYSTS FOR DIMETHYL ETHER SYNTHESIS FROM SYNGAS

Synergistic Effect of Zinc and Manganese in Cu-Mn-Zn/Y Catalyst for Syngas-to-dimethyl Ether

Effect of the Hydrogenation Components on Copper-Based Catalysts for Synthesis of Dimethyl Ether from CO2 Hydrogenation

Effect of the Addition of Manganese and Zinc on the Properties of Copper-Based Catalyst for the Synthesis of Syngas to Dimethyl Ether

Characterization of Cu-Mn/Zeolite-Y Catalyst for One-Step Synthesis of Dimethyl Ether from Co-H-2

Direct Synthesis of Dimethyl Ether on Supported Cu-Mn Catalysts

Synthesis of Dimethyl Ether on Supported Cu-Mn Catalysts

HYDROGENATION ON SUPPORTED Cu-Mn-ZnOX CATALYST--EFFECT OF PREPARATION METHOD AND REACTION CONDITIONS

Mechanism and catalytic performance for direct dimethyl ether synthesis by CO2 hydrogenation over CuZnZr/ferrierite hybrid catalyst

Dme Synthesis From Co/H-2 Over Cu-Mn/Gamma-Al2o3 Catalyst

DME Synthesis From CO/H<sub>2</sub> over Cu-Mn/Ă-Al<sub>2</sub>O<sub>3</sub> Catalyst

DME Synthesis From CO/H 2 over Cu-Mn/Ă-Al 2 O 3 Catalyst

Dimethyl Ether Synthesis Via Methanol and Syngas over Rare Earth Metals Modified Zeolite Y and Dual Cu–Mn–Zn Catalysts

Synthesis of Dimethyl Ether (DME) on Modified HY Zeolite and Modified HY Zeolite-Supported Cu–Mn–Zn Catalysts

Dimethyl Ether Synthesis from Methanol and Syngas over Different Sized HY Zeolite and Cu-Mn-Zn/HY Bifunctional Catalyst

Effect of Composition of Raw Materials on Structure and Dimethyl Ether Synthesis Activity of Cu-Zn-Al Catalyst Prepared by Complete Liquid Phase Method

99/00320 Effect of oxide dispersion in a bifunctional catalyst on the formation of dimethyl ether

Catalysis for One-step Synthesis of Dimethyl Ether from Hydrogenation of CO