Selective Catalytic Reduction ofNOx by Methane over La(1-x)SrxMnO3 Perovskites
Sijia Huang,Duanyang Wang,Hang Zhang,Na Li,Qulan Zhou
DOI: https://doi.org/10.11715/rskxjs.R201301036
2013-01-01
Abstract:Powder perovskite-type La(1-x)SrxMnO3(x=0,0.2,0.4)were synthesized by sol-gel method,and supported La(1-x)SrxMnO3(x=0.2,0.4)were synthesized by excessive dipping method. The powders were characterized by XRD and SEM,and supported catalysts were then submitted to activity tests in the selective catalytic reduction(SCR)of NO by meth-ane with or without O2. The experimental results showed that the crystal structure of Sr-substituted samples was the charac-teristic perovskite structure,and what’s more,La0.8,Sr0.2,MnO3possessed a porous structure. In the absence of O2,the reduction of NOx by CH4 was performed over La0.8,Sr0.2,MnO3and La0.6,Sr0.4,MnO3,leading to a maximum of 90% at 800-900,℃. The catalytic performance of La0.8,Sr0.2,MnO3 could reach a maximum of 80% at 800,℃ with 6% O2,on the other hand,the performance of La0.6,Sr0.4,MnO3was suppressed by the presence of O2. The catalytic performance was improved by both La0.8,Sr0.2,MnO3and La0.6,Sr0.4,MnO3 at 500-600,℃.