Dynamic study on desulphurization reaction of MgO-CaO refractories

Lin Tian,Shujiang Chen,Ling Zhang
DOI: https://doi.org/10.3969/j.issn.1001-1935.2006.05.011
2006-01-01
Abstract:The MgO-CaO brick (w (MgO) = 75.13%, w (CaO) = 22.09%) was made into a crucible and dried. A prepared steel specimen was placed in the crucible and both were fired in a high temperature tube furnace in argon protective atmosphere. The temperature was raised to 1600 °C and then maintained for 5-70 minutes, the specimen was taken out every 5 min. The microstructure of the crucible and [S] content in the molten steel were analyzed by polarizing microscope and direct-reading spectrograph. A dynamic model of the desulphurization reaction of molten steel was made and the desulphurization dynamic mechanism of the magnesia-calcia refractories at 1600 °C was studied. The result indicated that the best effect of desulphurization with rate of 70.12% appeared when reaction lasted 45 min at 1600 °C; However, when the reaction lasted over 45 min, the desulphurization rate decreased and 'resulphurization' happened. The previous stage of desulphurization process was controlled by interface chemical reaction mechanics and the posterior stage was controlled by diffusion mechanics. The chemical reaction rate constant, K r = 5.50 × 10 -4 m · s -1 and the diffusion coefficient D eff = 1.33 × 10 -8 m 2 · s -1.
What problem does this paper attempt to address?