Abstract:A series of novel amphibious organic/inorganic hybrid proton exchange membranes with H3PO4 doped which could be used under both wet and dry conditions was prepared through a sol-gel process based on acrylated triethoxysilane(A-TES) and benzyltetrazole-modified triethoxysilane(BT-TES). The dual-curing approach including UV-curing and thermal curing was used to obtain the crosslinked membranes. Polyethylene glycol(400) diacrylate(PEGDA) was used as an oligomer to form the polymeric matrix. The molecular structures of precursors were characterized by H-1, C-13 and Si-29 NMR spectra. The thermogravimetric analysis(TGA) results show that the membranes exhibit acceptable thermal stability for their application at above 200 degrees C. The differential scanning calorimeter(DSC) determination indicates that the crosslinked membranes with the mass ratios of below 1.6 of BT-TES to A-TES and the same mass of H3PO4 doped as that of A-TES possess the To, and the lowest 75-28.9 degrees C) exists for the membrane with double mass of H3PO4 doped as well. The high proton conductivity in a range of 9.4-17.3 mS/cm with the corresponding water uptake of 19.1%-32.8% of the membranes was detected at 90 degrees C under wet conditions. Meanwhile, the proton conductivity in a dry environment for the membrane with a mass ratio of 2.4 of BT-TES to A-TES and double H3PO4 loading increases from 4.89x10(-2) mS/cm at 30 degrees C to 25.7 mS/cm at 140 degrees C. The excellent proton transport ability under both hydrous and anhydrous conditions demonstrates a potential application in the polymer electrolyte membrane fuel cells.

New anion exchanger organic-inorganic hybrid materials and membranes from a copolymer of glycidylmethacrylate and γ-methacryloxypropyl trimethoxy silane

New Anion Exchanger Organic-Inorganic Hybrid Materials And Membranes From A Copolymer Of Glycidylmethacrylate And Gamma-Methacryloxypropyl Trimethoxy Silane

Novel Anion-Exchange Organic–inorganic Hybrid Membranes Prepared Through Sol–gel Reaction of Multi-Alkoxy Precursors

Hybrid anion exchange hollow fiber membranes through sol–gel process of different organic silanes within BPPO matrix

Novel anion-exchange organic-inorganic hybrid membranes prepared through sol-gel reaction and UV/thermal curing

3-Glycidoxy-propylthrimethoxysilane Improved Anion Exchange Membranes Based on Quaternized Poly(2,6-Dimethyl-1,4-phenyleneoxide)

Novel polysulfone hybrid ultrafiltration membrane prepared with TiO2-g-HEMA and its antifouling characteristics

Inorganic-organic hybrid membranes with anhydrous proton conduction prepared from tetraethoxysilane, 3-glycidyloxypropyltrimethoxysilane, trimethyl phosphate and diethylethylammonium trifluoromethanesulfonate

Cation exchange hybrid membranes based on PVA for alkali recovery through diffusion dialysis

Synthesis and Characterizations of New Negatively Charged Organic–inorganic Hybrid Materials

Fundamental Studies of a New Hybrid (inorganic–organic) Positively Charged Membrane. II. Membrane Preparation Via Alcoholysis Reaction and Amination Processes of Silicone and Titanate Coupling Agents

Preparation and Characterization of Novel Negatively Charged Hybrid Membranes

Anion exchange hybrid membranes from PVA and multi-alkoxy silicon copolymer tailored for diffusion dialysis process

Fundamental studies of a new hybrid (inorganic–organic) positively charged membrane: membrane preparation and characterizations

Novel Hollow‐fiber Anion‐exchange Hybrid Membranes: Preparation and Characterization

Novel anion-exchange organic–inorganic hybrid membranes: Preparation and characterizations for potential use in fuel cells

Preparation of Organic–inorganic Hybrid Cation-Exchange Membranes Via Blending Method and Their Electrochemical Characterization

Pva-Based Hybrid Membranes From Cation Exchange Multisilicon Copolymer For Alkali Recovery

PVA–silica anion-exchange hybrid membranes prepared through a copolymer crosslinking agent

Preparation and Conducting Behavior of Amphibious Organic/Inorganic Hybrid Proton Exchange Membranes Based on Benzyltetrazole

Proton-conductive inorganic–organic hybrid membranes synthesized from a trimethoxysilylmethylstyrene–fluorophenylvinyl acid copolymer