Fundamental Studies of a New Hybrid (inorganic–organic) Positively Charged Membrane. II. Membrane Preparation Via Alcoholysis Reaction and Amination Processes of Silicone and Titanate Coupling Agents

JS Liu,TW Xu,M Gong,YX Fu

DOI: https://doi.org/10.1016/j.memsci.2005.03.058

IF: 9.5

2005-01-01

Journal of Membrane Science

Abstract:A series of novel inorganic–organic hybrid positively charged membranes were prepared by coupling of 3-glycidoxypropyltrimethoxysilane (GPTMS) and mixed GPTMS/Ti(O-n-C4H9)4 in n-butyl alcohol (BuOH) solution at various temperatures and then followed quaternary amination with trimethyl amine (TMA). The synthesized membranes were characterized by IEC, streaming potential, pure water flux, FT-IR, TGA measurements as well as SEM observations. It was exhibited that anion exchange capacities (IECs) of the membranes decreased with increasing curing temperature within a range of (1.4–3.1)×10−2mequiv.cm−2 coated for one time and (3.5–4.6)×10−2mequiv.cm−2 coated for two times. The positive charge of the membranes was approved by these IEC values as well as FT-IR spectrum of step products and streaming potential values. The thermal stability was tested by TGA analysis and showed that the membranes doped with titanium could undergo a curing temperature up to 300°C. Pure water flux showed that they decreased with increasing curing temperature, the composition of precursor and dip-coating times, respectively. SEM observations indicated that the membranes became thicker and denser with increasing content of titanium, but excessive Ti-content would decrease the stability of SiOTi bonds in the membranes.