Abstract:It is a plaguing problem of obtaining high ion flux while maintaining high selectivity during the diffusion dialysis (DD) process. However, functionalized mesoporous silica-based composite membrane is considered to be one of the effective candidates to solve it. Here, we report amino-modified mesoporous silica (AMMS) blended with pre-crosslinked polyvinyl alcohol (PVA) solution, after which a series of composite membranes were obtained to maintain high ion flux and selectivity. The fundamental properties of as-prepared membranes were tested, including water uptake (W R ), alkali resistance, mechanical and thermal properties. The results of W R (181.7%–289.7%), alkali resistance (with swelling degree in the range of 250%–471% and mass loss in the range of 27.6%–35.3%), mechanical (with tensile strength (TS) in the range of 29.9–41.8 MPa and elongation at break (E b ) in the range of 135.3%–180.4%), and thermal (degradation temperature was higher than 200 o C) properties demonstrated that the as-prepared membranes possess higher water uptake and moderate alkali resistance and can be potentially applied in alkaline DD process. Further, microscopic morphologies of as-prepared membranes confirmed well dispersion of AMMS in PVA matrix and good compatibility between the two phases, which could be attributed to the hydrogen bonding between –NH 2 of AMMS and –OH of PVA molecular. NaOH/Na 2 WO 4 system was introduced to evaluate separation performance of as-prepared membranes via DD process and the effect of AMMS was detected preliminarily. The results indicated that amino-modified mesoporous silica (AMMS) blended with pre-crosslinked polyvinyl alcohol (PVA) membrane possessed high ion flux and selectivity simultaneously, and had strong practical application prospects. The mesopores and –NH 2 groups of AMMS promoted the transport of OH − via hydrogen bonds synergistically.

Anion exchange hybrid membranes from PVA and multi-alkoxy silicon copolymer tailored for diffusion dialysis process

Cation exchange hybrid membranes based on PVA for alkali recovery through diffusion dialysis

PVA/SiO 2 anion exchange hybrid membranes from multisilicon copolymers with two types of molecular weights

Cation exchange hybrid membranes from SPPO and multi-alkoxy silicon copolymer: Preparation, properties and diffusion dialysis performances for sodium hydroxide recovery

Carboxylic acid type PVA-based hybrid membranes for alkali recovery using diffusion dialysis

Pva-Based Hybrid Membranes From Cation Exchange Multisilicon Copolymer For Alkali Recovery

Poly (aryl Ether Ketone)/polymeric Ionic Liquid with Anisotropic Swelling Behavior for Anion Exchange Membranes

Preparation of cation-exchange hybrid membranes with multi-functional groups and their performance on alkali recovery

Cation Exchange PVA/SPPO/SiO2 Membranes with Double Organic Phases for Alkali Recovery

Zwitterionic Multisilicon Copolymer Used for Preparing PVA Based Hybrid Membranes for Alkali Recovery

Double Cross-Linking PVA-SiO2 Hybrid Membranes for Alkali Recovery

PVA-based Cation Exchange Hybrid Membranes with Multifunctional Groups Prepared from Ternary Multisilicon Copolymer

The Effects of Multi-Functional Groups from PVA and Ternary Multisilicon Copolymer on Diffusion Dialysis

Diffusion dialysis of hydrochloride acid at different temperatures using PPO–SiO2 hybrid anion exchange membranes

Crosslinked Pva-Based Hybrid Membranes Containing Di-Sulfonic Acid Groups for Alkali Recovery

Porous BPPO-based Membranes Modified by Multisilicon Copolymer for Application in Diffusion Dialysis

A novel UV-crosslinked sulphonated polysulfone cation exchange membrane with improved dimensional stability for electrodialysis

Alkali recovery using PVA/SiO2 cation exchange membranes with different -COOH contents.

Preparation and properties of polyvinyl alcohol (PVA)/amino-modified mesoporous silica (AMMS) composite membranes for diffusion dialysis

Facile and Cost Effective PVA Based Hybrid Membrane Fabrication for Acid Recovery

Novel Composite Anion Exchange Membranes Based on Quaternized Polyepichlorohydrin for Electromembrane Application