Abstract:It is a plaguing problem of obtaining high ion flux while maintaining high selectivity during the diffusion dialysis (DD) process. However, functionalized mesoporous silica-based composite membrane is considered to be one of the effective candidates to solve it. Here, we report amino-modified mesoporous silica (AMMS) blended with pre-crosslinked polyvinyl alcohol (PVA) solution, after which a series of composite membranes were obtained to maintain high ion flux and selectivity. The fundamental properties of as-prepared membranes were tested, including water uptake (W R ), alkali resistance, mechanical and thermal properties. The results of W R (181.7%–289.7%), alkali resistance (with swelling degree in the range of 250%–471% and mass loss in the range of 27.6%–35.3%), mechanical (with tensile strength (TS) in the range of 29.9–41.8 MPa and elongation at break (E b ) in the range of 135.3%–180.4%), and thermal (degradation temperature was higher than 200 o C) properties demonstrated that the as-prepared membranes possess higher water uptake and moderate alkali resistance and can be potentially applied in alkaline DD process. Further, microscopic morphologies of as-prepared membranes confirmed well dispersion of AMMS in PVA matrix and good compatibility between the two phases, which could be attributed to the hydrogen bonding between –NH 2 of AMMS and –OH of PVA molecular. NaOH/Na 2 WO 4 system was introduced to evaluate separation performance of as-prepared membranes via DD process and the effect of AMMS was detected preliminarily. The results indicated that amino-modified mesoporous silica (AMMS) blended with pre-crosslinked polyvinyl alcohol (PVA) membrane possessed high ion flux and selectivity simultaneously, and had strong practical application prospects. The mesopores and –NH 2 groups of AMMS promoted the transport of OH − via hydrogen bonds synergistically.

Alkali recovery using PVA/SiO2 cation exchange membranes with different -COOH contents.

Cation exchange hybrid membranes based on PVA for alkali recovery through diffusion dialysis

Carboxylic acid type PVA-based hybrid membranes for alkali recovery using diffusion dialysis

Pva-Based Hybrid Membranes From Cation Exchange Multisilicon Copolymer For Alkali Recovery

Cation Exchange PVA/SPPO/SiO2 Membranes with Double Organic Phases for Alkali Recovery

Zwitterionic Multisilicon Copolymer Used for Preparing PVA Based Hybrid Membranes for Alkali Recovery

Double Cross-Linking PVA-SiO2 Hybrid Membranes for Alkali Recovery

Preparation of cation-exchange hybrid membranes with multi-functional groups and their performance on alkali recovery

Anion exchange hybrid membranes from PVA and multi-alkoxy silicon copolymer tailored for diffusion dialysis process

Cation exchange hybrid membranes from SPPO and multi-alkoxy silicon copolymer: Preparation, properties and diffusion dialysis performances for sodium hydroxide recovery

Development of Pva/Mida Based Hybrid Cation Exchange Membranes for Alkali Recovery Via Diffusion Dialysis

The Effects of Multi-Functional Groups from PVA and Ternary Multisilicon Copolymer on Diffusion Dialysis

Poly (aryl Ether Ketone)/polymeric Ionic Liquid with Anisotropic Swelling Behavior for Anion Exchange Membranes

Crosslinked Pva-Based Hybrid Membranes Containing Di-Sulfonic Acid Groups for Alkali Recovery

PVA/SiO 2 anion exchange hybrid membranes from multisilicon copolymers with two types of molecular weights

Cation exchange hybrid membranes prepared from PVA and multisilicon copolymer for application in alkali recovery

A Simple and Green Preparation of Pva-Based Cation Exchange Hybrid Membranes for Alkali Recovery

Preparation of a Cation Exchange Membrane by a Sol-Gel Method-Based Polyvinyl Alcohol to Improve Alkali Recovery via Diffusion Dialysis in the Textile Industry

Fabrication of Cation Exchange Membrane from Polyvinyl Alcohol Using Lignin Sulfonic Acid: Applications in Diffusion Dialysis Process for Alkali Recovery

PVA-based Cation Exchange Hybrid Membranes with Multifunctional Groups Prepared from Ternary Multisilicon Copolymer

Preparation and properties of polyvinyl alcohol (PVA)/amino-modified mesoporous silica (AMMS) composite membranes for diffusion dialysis