Abstract:Poly(propylene carbonate) (PPC) was implanted by oxygen ion with energy of 40keV. The influence of experimental parameters was investigated by varying ion fluence from 1×1012 to 1×1015ions/cm2. XPS, SEM, surface roughness, wettability, hardness, and modulus were employed to investigate structure and properties of the as-implanted PPC samples. Eight chemical groups, i.e., carbon, CH, COC, CO, OCO, CO, , and groups were observed on surfaces of the as-implanted samples. The species and relative intensities of the chemical groups changed with increasing ion fluence. SEM images displayed that irradiation damage was related strongly with ion fluence. Both surface-recovering and shrunken behavior were observed on surface of the PPC sample implanted with fluence of 1×1015ions/cm2. As increasing ion fluence, the surface roughness of the as-implanted PPC samples increased firstly, reached the maximum value of 159nm, and finally decreased down the minimum value. The water droplet contact angle of the as-implanted PPC samples changed gradually with fluence, and reached the minimum value of 70° with fluence of 1×1015ions/cm2. The hardness and modulus of the as-implanted PPC samples increased with increasing ion fluence, and reached their corresponding maximum values with fluence of 1×1015ions/cm2. The experimental results revealed that oxygen ion fluence closely affected surface chemical group, morphology, surface roughness, wettability, and mechanical properties of the as-implanted PPC samples.

Study of absorption spectra of PC films irradiated by MeV C ions and C2+ cluster ions

The XPS Investigation on the PC Films Irradiated by MeV Cn+ (n = 1–5) Cluster Ions

The investigation of energy loss and damage in polycarbonate induced by MeV carbon clusters

Damage cross-section of carbon cluster ions Cn + (n = 1-5) collision with polycarbonate

Structural Investigation And Barrier Properties Of A-C : H Thin Films On Polymer By Pecvd

Spectral study of SiO2 photonic crystal under MeV Au ion irradiation

Evolution of optical properties and molecular structure of PCBM films under proton irradiation

Modification of Surface Mechanical Properties of Polycarbonate by B+ and O+ Ions Implantation

A comparative study on the effects induced following xenon ion implantation at high energies on the electrical, morphological and optical properties of CuInSe 2 monocrystalline

Studies on Ion-Implantation and Electrical-Properties of Polyacetylene Films

Mechanical Properties and Structure Evolution of Single-Crystalline Silicon Irradiated by 1 MeV Au+ and Cu+ Ions

Surface and Interface Properties of Ion Implanted 4H-Silicon Carbide

Investigation on CR39 implanted by Cn+ (n=1- 5) cluster ions

Impact of gamma irradiation on optical and nonlinear properties of Indium Chloride Phthalocyanine thin films

Surface Modification of Poly(propylene Carbonate) by Oxygen Ion Implantation

Au+ irradiation regulated surface defects and dielectric properties of CaCu3Ti4O12/CoFe2O4/epoxy composites

Structure Characterization of Modified Polyimide Films Irradiated by 2 MeV Si Ions

Implantation Study of Carbon Clusters Cn+(n=1—5) into NaCl Crystal

Reverse Saturable Absorption and Optical Limiting Performance of Fullerene-Functionalized Polycarbonates in Femtoseond Time Scale

Investigation into the Characteristics of A-C:H Films Irradiated by Electron Beam

MECHANISM OF WEAR RESISTANCE ON ENERGETIC ION IMPLANTED POLYMER FILMS