Surface Modification of Poly(propylene Carbonate) by Oxygen Ion Implantation
Jizhong Zhang,Jiachen Kang,Ping Hu,Qingli Meng
DOI: https://doi.org/10.1016/j.apsusc.2006.12.023
IF: 6.7
2006-01-01
Applied Surface Science
Abstract:Poly(propylene carbonate) (PPC) was implanted by oxygen ion with energy of 40keV. The influence of experimental parameters was investigated by varying ion fluence from 1×1012 to 1×1015ions/cm2. XPS, SEM, surface roughness, wettability, hardness, and modulus were employed to investigate structure and properties of the as-implanted PPC samples. Eight chemical groups, i.e., carbon, CH, COC, CO, OCO, CO, , and groups were observed on surfaces of the as-implanted samples. The species and relative intensities of the chemical groups changed with increasing ion fluence. SEM images displayed that irradiation damage was related strongly with ion fluence. Both surface-recovering and shrunken behavior were observed on surface of the PPC sample implanted with fluence of 1×1015ions/cm2. As increasing ion fluence, the surface roughness of the as-implanted PPC samples increased firstly, reached the maximum value of 159nm, and finally decreased down the minimum value. The water droplet contact angle of the as-implanted PPC samples changed gradually with fluence, and reached the minimum value of 70° with fluence of 1×1015ions/cm2. The hardness and modulus of the as-implanted PPC samples increased with increasing ion fluence, and reached their corresponding maximum values with fluence of 1×1015ions/cm2. The experimental results revealed that oxygen ion fluence closely affected surface chemical group, morphology, surface roughness, wettability, and mechanical properties of the as-implanted PPC samples.