Study on preparation of nano-Cu powders by hydrogen reducing

Zaiyuan Li,Chengyan Liu,Yuchun Zhai,Haiying Liu
2006-01-01
Abstract:The 0.1 mol·L-1 CuSO4 liquor and 4 mol·L-1 NaOH liquor were prepared by CuSO4·5H2O and NaOH as raw materials. The nano-Cu(OH)2 were prepared by chemical precipitation. The Cu nano-powders was prepared with Cu(OH)2 nanofibers by seal circulation hydrogen restores system. The result indicate that the nano-Cu(OH)2 have a diameter of 10-30 nm and a length of 1-6 μm. The reaction conditions were: the concentration of CuSO4 solution was 0.1 mol·L-1, that of NaOH solution was 4 mol·L-1, the dropping rate of NaOH solution was 50 ml ·min-1, the reaction temperature was 25°C, the pH value of the reaction end was larger than 12, the stirring rate was 1200 r·min-1. The system easily judged destination of the reaction. The time of Cu nano-powders in constant temperature area was reduced and the size of the pellet was prevented from growing up. The hydrogen reducing of Cu(OH)2 nano-powders temperature was 240°C, the time was 6 min. The Cu particle size was 50-80 nm. Purity was 99.06%.
What problem does this paper attempt to address?