Abstract:A simple method was put forward in this paper for preparing colloidal copper nanoparticles in aqueous solutions using copper sulfate, gum acacia and hydrazine hydrate as copper precursor, capping agents and reducing agents, respectively, without any inert gas. The formation of nanosized copper was confirmed by its characteristic surface plasmon absorption peak at 604nm in UV–vis spectra. The transmission electron microscopic (TEM) and scanning electron microscope (SEM) images show that the as-synthesized copper fine spherical particles are distributed uniformly with a narrow distribution from 3nm to 9nm. The X-ray diffraction (XRD) and high resolution transmission electron microscopic (HRTEM) demonstrated that the obtained metallic nanoparticles are single crystalline copper nanoparticles. Fourier transform infra-red (FT-IR) spectroscopic data suggested that the copper nanoparticles are coated with gum acacia. The effects of the quantity of gum acacia on the particle size were investigated by the UV–vis spectra and TEM images. The growth process of the nanoparticles was monitored by the UV–vis spectra. The mechanism of the formation copper nanoparticles was discussed. The process raised in this study can be served as an excellent candidate for the preparation of copper nanoparticles in a large scale production.

Preparation of Monodispersed Copper Nanoparticles by an Environmentally Friendly Chemical Reduction

Synthesis of Well-Dispersed Copper Nanoparticles by L-Ascorbic Acid in Diethyleneglycol

Synthesis of Copper Nanoparticles by L-ascorbic Acid at Room Temperature

Synthesis of Ultrafine Copper Particles by Complex-Reduction-Extraction Method

A Simple and Novel Method for Large-Scale Preparation of Stable Copper Nanoparticles

Preparation of copper nano-particle by homogeneous reduction method

Preparation and Self-Assembly of Copper Nanoparticles Via Discharge of Copper Rod Electrodes in a Surfactant Solution: a Combination of Physical and Chemical Processes

Preparation of Micron Size Copper Powder with Chemical Reduction Method

Facile Fabrication of Ultrafine Copper Nanoparticles in Organic Solvent

Preparation of Copper Nanoparticles with Low Sintering Temperature

Preparation of Copper Nanoparticles with Liquid Reduction Method by Sodium Hypophosphite

Preparation of copper nanoparticles in a water/oleic acid mixed solvent via two-step reduction method

Synthesis and Characterization of Monodisperse Copper Nanoparticles Using Gum Acacia

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Preparation of Copper Nanoparticles by Chemical Reduction Method Using Potassium Borohydride

Preparation of Copper Nanoparticles by Radiation

Facile Electrochemical Synthesis of Single-Crystalline Copper Nanospheres, Pyramids, and Truncated Pyramidal Nanoparticles from Lithia/Cuprous Oxide Composite Thin Films

Size Distribution Control of Copper Nanoparticles and Oxides: Effect of Wet-Chemical Redox Cycling

Synthesis of Size-Controlled Pure Copper Nanoparticles for Packaging Interconnect

Preparation of Fine Copper Powder with Chemical Reduction Method and Its Application in Mlcc

Size Refinement of Copper Nanoparticles: A Perspective from Electrochemical Nucleation and Growth Mechanism