Abstract:Ultrafine copper powders were prepared by the air-jet milling of copper oxide (CuO) powders and a subsequent hydrogen (H2) reduction. After milling, the particle size and grain size of CuO powders decreased, while the specific surface area and structural microstrain increased, thereby improving the reaction activity. In a pure H2 atmosphere, the process of CuO reduction was conducted in one step, and followed a pseudo-first-order kinetics model. The smaller CuO powders after milling exhibited higher reduction rates and lower activation energies compared with those without milling. Based on the unreacted shrinking core model, the reduction of CuO powders via H2 was controlled by the interface reaction at the early stage, whereas the latter was limited by the diffusion of H2 through the solid product layer. Additionally, the scanning electron microscopy (SEM) indicated that copper powders after H2 reduction presented a spherical-like shape, and the sintering and agglomeration between particles occurred after 300 °C, which led to a moderate increase in particle size. The preparing parameters (at 400 °C for 180 min) were preferred to obtain ultrafine copper powders with an average particle size in the range of 5.43–6.72 μm and an oxygen content of less than 0.2 wt.%.

Preparation of copper nano-particle by homogeneous reduction method

Preparation of Copper Nanoparticles with Low Sintering Temperature

Preparation of Monodispersed Copper Nanoparticles by an Environmentally Friendly Chemical Reduction

Preparation of ZnO/SiO_2 Nanoparticle by Adsorption Phase Reaction Technique

Synthesis of CuO/SiO2 nanocomposite material using adsorption method

Progress in Preparation of Ultrafine Copper Powder by Chemical Reduction Method

Preparation and microstructure of nano-sized Cu particles by mechanochemical reaction

Facile Fabrication of Ultrafine Copper Nanoparticles in Organic Solvent

Preparation of ultrafine copper powders by NH2NH2 center dot H2O-HCHO direct reduction method and glucose prereruction method

Preparation of Copper Nanoparticles by Radiation

Preparation of Copper Nanoparticles on Carbon Nanotubes by Electroless Plating Method

Preparation and optical properties of Cu2O hollow microsphere film and hollow nanosphere powder via a simple liquid reduction approach

One-Pot Fast Synthesis of Leaf-Like CuO Nanostructures and CuO/Ag Microspheres with Photocatalytic Application

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Diameter and Aggregation Controlled Preparation by Solvothermal Synthesis of Ultra-small Particles CuFe$_2$O$_4$

The Preparation of an Ultrafine Copper Powder by the Hydrogen Reduction of an Ultrafine Copper Oxide Powder and Reduction Kinetics

A simple method for the preparation of Cu 20 with different morphologies in high reaction concentrations

Preparation and Investigation on Copper Nanoparticles in Conductive Ink

Sequential Two-Step Reduction of High-Purity Nano Copper with Glucose and Ascorbic Acid for the Synthesis of Nano Silver-Coated Copper

Synthesis of Copper Nanocolloids Using A Continuous Flow Based Microreactor

High Purity Copper Nanoparticles Via Sonoelectrochemical Approach