Abstract:High crystallinity copper nanoparticles are synthesized by a novel simple route at low temperatures under a measurable condition of altering the medium of the reaction. The effect of altering the reaction medium on reducing the surface energy of precursors to form high crystalline copper nanoparticles from their sulphate precursors due to facilities for the capping of nanoparticles is studied in this manuscript. In this observation, copper sulfate pentahydrate (CSP) precursors follow a reduction in the presence of ascorbic acid (reducer) and their crystallinity gradually changes up to 100 % while the CSP medium is water (X), methanol (Y) and water-methanol azeotropic mixture (Z), respectively. XRD identified a pure 100 % metallic copper crystalline phase presence in Y. Exhaustive lattice parameters, peak profiling, lattice constant etc. analysis of the conformation. TGA data ensures the oxidation initiation of pure Cu to CuO at an initial 30 °C, while the calculated activation energy is 27.93 KJ/mol of Y. An outstanding approach in XRD as well as TEM shows that the average size of the particle close to 16 to 78 nm depends on the solvent medium. Furthermore, TEM-couple SAED parallelly proves this consists of miller indices (111), (200) and (220) in X, Y but Z in a single crystal of metallic copper phase for the phenomenon of parallel line diffraction. TEM shows the internal spherical shape of the nanoparticles varies from the medium with the regular arrangement in a uniform distribution that consists of very low agglomeration. EDS confirms highly purified copper nanomaterials in Y is 83 % among the X and Z. The operating process could be applied to synthesize and integrate the crystallinity, particle size and crystal shape of different metallic nanoparticles by alternating the reaction medium.

Preparation of Copper Nanoparticles with Low Sintering Temperature

Copper nanoparticles: aqueous phase synthesis and conductive films fabrication at low sintering temperature.

A mild aqueous synthesis of ligand-free copper nanoparticles for low temperature sintering nanopastes with nickel salt assistance

Study on the Resistivity and Porosity of Nano Copper Powder Under Low-Temperature Sintering without Pressure

Preparation of copper nano-particle by homogeneous reduction method

A Simple and Novel Method for Large-Scale Preparation of Stable Copper Nanoparticles

Ambient Aqueous-Phase Synthesis of Copper Nanoparticles and Nanopastes with Low-Temperature Sintering and Ultra-High Bonding Abilities

Preparation of Copper Nanoparticles by Radiation

Synthesis of Copper Nanoparticles by L-ascorbic Acid at Room Temperature

Preparation of Monodispersed Copper Nanoparticles by an Environmentally Friendly Chemical Reduction

Preparation of Copper Nanoparticles with Liquid Reduction Method by Sodium Hypophosphite

Preparation and Self-Assembly of Copper Nanoparticles Via Discharge of Copper Rod Electrodes in a Surfactant Solution: a Combination of Physical and Chemical Processes

Synthesis and Characterization of Highly-Dispersed Copper Submicron Particles for Low Temperature Sintering Joints

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

The Synthesis of Copper Nanoparticles for Printed Electronic Materials Using Liquid Phase Reduction Method

Preparation of Micron Size Copper Powder with Chemical Reduction Method

Synthesis and crystallinity integration of copper nanoparticles by reaction medium

High Purity Copper Nanoparticles Via Sonoelectrochemical Approach

Microwave-assisted Synthesis of Mo–Cu Nano-Powders at an Ultra-Low Temperature and Their Sintering Properties

Low Temperature Bonding of Cu Metal through Sintering of AgNanoparticles for High Temperature Electronic Application

Synthesis and Characterization of Monodisperse Copper Nanoparticles Using Gum Acacia