Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Preparation of CuO-Ag/SiO2 nano-composites via adsorption phase reaction technique

Synthesis of CuO/SiO2 nanocomposite material using adsorption method

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

Preparation of ZnO/SiO_2 Nanoparticle by Adsorption Phase Reaction Technique

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

Influence of copper species on silver grain size in Ag–CuO–SiO2 ternary nanocomposites

Effect of adsorption layer on preparation process of Ag/SiO2 nanocomposite materials

Adsorption phase synthesis: preparation of nanoparticles and the effects of reactant distribution.

Influence of adsorption of reactants on preparation of silver nanoparticles by adsorption phase synthesis

Studies on Preparation of Ag/SiO2 Nanocomposite and Its Electrical Properties

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Study on the regulation of the absorbate's distribution and its effect on the size of the nanoparticles during the preparation of Cu/SiO2

Influence of Reactant on Preparation of NiO/SiO_2 Via Adsorption Phase Reaction Technique

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Preparation of Nanometer Tio2/Sio2 Composite Materials by Adsorption Phase Nanoreactor Technique

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Preparation of Au Nanoparticles on Surface of Two Supports by Adsorption Phase Synthesis

Preparation of Ag-Al2O3 nano-composites powder

Effects of Ag Nanoparticles on the Visible-Light-driven Photocatalytic Properties of Cu2O Nanocubes

Preparation of AgSnO2 Nano-Composite Powder by Wet Chemical Method