Abstract:The impact of a titania (TiO2) support film surface on the catalytic activity of gold nanoparticles (Au NP) was investigated. Using the reactive dc-magnetron sputtering technique, TiO2 films with an amorphous, anatase, and nitrogen-doped anatase crystal structure were produced for a subsequent role as a support material for Au NP. Raman spectra of these TiO2 films revealed that both vacuum and NH3 annealing treatments promoted amorphous to anatase phase transformation through the presence of a peak in the 513-519 cm-1 spectral regime. Furthermore, annealing under NH3 flux had an associated blue shift and broadening of the Raman active mode at 1430 cm-1, characteristic of an increase in the oxygen vacancies (VO). For a 3 to 15 s sputter deposition time, the Au NP over TiO2 support films were in the 6.7-17.1 nm size range. From X-ray photoelectron spectroscope (XPS) analysis, the absence of any shift in the Au 4f core level peak implied that there was no change in the electronic properties of Au NP. On the other hand, spontaneous hydroxyl (-OH) group adsorption to anatase TiO2 support was instantly detected, the magnitude of which was found to be enhanced upon increasing the Au NP loading. Nitrogen-doped anatase TiO2 supporting Au NP with ~21.8 nm exhibited a greater extent of molecular oxygen adsorption. The adsorption of both -OH and O2 species is believed to take place at the perimeter sites of the Au NP interfacing with the TiO2 film. XPS analyses and discussions about the tentative roles of O2 and -OH adsorbent species toward Au/TiO2 systems corroborate very well with interpretations of density functional theory simulations.

Preparation of Au Nanoparticles on Surface of Two Supports by Adsorption Phase Synthesis

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Preparation of Au Catalyst on Modified Sio2 Via Adsorbed-Layer Nanoreactor Technique

Influence of Reactant on Preparation of NiO/SiO_2 Via Adsorption Phase Reaction Technique

Adsorption phase synthesis: preparation of nanoparticles and the effects of reactant distribution.

Preparation of Tio2 Nanoparticles on Surface of Different Supports by Adsorption Phase Reaction Technique

Preparation of Tio2 Nanoparticles on Different Sio2 Supports by the Adsorption Phase Technique

Influence of adsorption of reactants on preparation of silver nanoparticles by adsorption phase synthesis

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

Preparation of ZnO/SiO_2 Nanoparticle by Adsorption Phase Reaction Technique

Preparation of CuO-Ag/SiO2 nano-composites via adsorption phase reaction technique

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Preparation of TiO2 nanoparticles on the surface of SiO2 in binary liquids

Preparation of SiO2@Au@TiO2 Core–shell Nanostructures and Their Photocatalytic Activities under Visible Light Irradiation

X-ray Photoelectron Spectroscopy (XPS) Analysis of Ultrafine Au Nanoparticles Supported over Reactively Sputtered TiO2 Films

Low-Temperature Solution-Phase Synthesis of NiAu Alloy Nanoparticles Via Butyllithium Reduction: Influences of Synthesis Details and Application As the Precursor to Active Au-NiO/SiO2 Catalysts Through Proper Pretreatment

Preparation and Characterization of Ag Nanoparticles Embedded in Hierarchically Porous Monolithic Silica

Fabrication of Designed Architectures of Au Nanoparticles on Solid Substrate with Printed Self-Assembled Monolayers As Templates

Synthesis of Stable Au–SiO2 Composite Nanospheres with Good Catalytic Activity and SERS Effect