Abstract:The uniformity of the cell size of aluminum foams prepared by traditional melt foaming and gas injection methods is difficult to control. In order to improve the controllability of cell size and mechanical performance of aluminum foam, an A356 matrix syntactic foam was prepared by the improved stir casting process. Moreover, the compressive property of the syntactic foam was studied and compared with other metal foams. Al2O3 hollow spheres with the diameters of 3-5mm were added in the molten A356 alloy, then the syntactic foam can be obtained after stirring and compaction. The hollow spheres in the syntactic foam are random loose packed. The volume fraction of 3-3.5 mm hollow spheres in the syntactic foam could reach to 56%. The total densities of the syntactic foams are around 1.79 g/cm(3). Through the analysis both in macroscopic and microscopic, the interfacial bonding between aluminum matrix and hollow spheres was proved to be good even after mechanical cutting. The quasi-static compression result showed that the plateau stress of the syntactic foam with 3-3.5mm hollow spheres could reach up to 46 MPa, and the corresponding densification strain energy is 20 MJ/m(3). Moreover, the plateau region is flat, long and relatively high. The syntactic foam with the hollow spheres of 3-4 mm diameter has the highest overall porosity and the best compressive performance. Compared with other traditional aluminum foams, this syntactic foam has advantages in energy absorption performance and the adjustability of cell size.

EFFECT OF MATRIX PROPERTIES ON THE MECHANICAL BEHAVIORS OF ALUMINUM FOAMS

Cell-size effect on mechanical properties of aluminum foams

Experiment research on the dynamic mechanical behavior of aluminum matrix syntactic foam

Preparation and Compressive Performance of an A356 Matrix Syntactic Foam

Micro-CT in the mechanical properties and energy absorption of closed-cell aluminium foam

Mechanical Properties of Aluminium Foam and How Density, Temperature, and Strain Rate Affect Dynamic Strain–Stress Relationship

High temperature and mesostructure effect on aluminum foam compression responses

Interface characterization and mechanical property of an aluminum matrix syntactic foam with multi-shelled hollow sphere structure

Dynamic mechanical properties of aluminum alloy foams

Experimental and Numerical Study on Strain Rate Effects of Close-Celled Aluminum Foams

Effects of cell wall property on compressive performance of aluminum foams

Microstructure and Compressive Properties of Aluminum Foams Made by 6063 Aluminum Alloy and Pure Aluminum

Dynamic Compressive Behavior of Aluminum Matrix Syntactic Foam and Its Multilayer Structure

Mechanical Properties of Aluminium Matrix Syntactic Foams Manufactured with Aluminium Smelter Waste

Dynamic mechanical properties of closed-cell aluminum foams with uniform and graded densities

Effect of Cell Diameter Variations on the Mechanical Behavior of Aluminum Foams: Experiments and Modeling

Dynamic Energy Absorption Property of Closed-Cell Aluminum Foam with Al Matrix and Al-6Si Matrix

Experimental investigation on the strain-rate effect and inertia effect of closed-cell aluminum foam subjected to dynamic loading

Compressive behavior and energy absorption analysis of casting skin-wrapped aluminum foams

Mechanical Properties of Porous Metallic and Natural Foams

Influence of Cell Wall Material and Cell Numbers on Mechanical Properties of Closed-Cell Aluminum Foams