Abstract:Electrochemical deposition (ED) has been proposed as a low temperature approach for preparing hydroxyapatite (HA) coatings. To overcome the problem of low adhesion, the preparation of thin and low-porosity coatings on Ti substrates pre-treated by micro-arc oxidation (MAO) is a good strategy. In this paper, a thin and dense HA coating was obtained by modifying parameters at pH 6.4, 45 °C, and 0.5 mA·cm −2 . The growth behaviours of HA electrodeposited on MAO coatings were investigated by SEM and EDS technology and summarized that the HA was initially generated in the MAO micropores, then covered the entire MAO surface and gradually grew outwards. This growth pattern was also confirmed by ATR-FTIR, XPS, EIS, open potential, and wettability results at different ED cycles. Adjusting 1:1 power-on/off time ratio affected the morphology of HA grown in the pores in the early stage and also increased the interfacial strength, up to 10.69 MPa at duty cycle 12/24.The cross-section of the final specimen was characterised by TEM and EDS, indicating that amorphous layers, nanocrystalline HA, and submicron HA were formed sequentially from the TiO 2 (Ca)/HA interface outwards. The increase in Ca 2+ concentration and the formation of CaO bonds at the interface may be important reasons for the adhesive enhancement. This process provides a strategy to enhance the strength of bioceramic materials on Ti substrates.

A study on controllable preparation of nano-hydroxyapatite coatings on Ti substrate by electrochemical deposition

Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate

A Novel Method to Synthesize Hydroxyapatite Coating with Hierarchical Structure

Synthesis and Characterization of Zn-substituted Hydroxyapatite Coatings by Electrochemical Deposition

Effect of Supersaturation on the Morphology of Hydroxyapatite Crystals Deposited by Electrochemical Deposition on Titanium

Synthesized Silicon-Substituted Hydroxyapatite Coating on Titanium Substrate by Electrochemical Deposition

Morphologies of Hydroxyapatite Crystal Deposited on Titanium Surface with Electrochemical Technique

Electrodeposition of Hydroxyapatite Coating on CoNiCrMo Substrate in Dilute Solution

Effect of EDTA on Electrodeposition of Hydroxyapatite Coatings

Electrolytic Deposition of Hydroxyapatite Coating on CoNiCrMo Substrates

Effect of Trisodium Citrate on Electrolytic Deposition of Hydroxyapatite Coatings

Ribbon-like and rod-like hydroxyapatite crystals deposited on titanium surface with electrochemical method

Preparation of hydroxyapatite coating on smooth implant surface by electrodeposition

Preparation and biological evaluation of Nano-HA coating on tatinium surfaces

Preparation and growth behaviours of low porosity hydroxyapatite with enhanced adhesion by electrochemical deposition on micro-arc oxide coatings

Electrolytic Deposition of Calcium Phosphate Coatings on Titanium Substrate

Preparation of Calcium Phosphate Coating on Titanium Alloy Substrate and Its Mechanism Study

Electrohydrodynamic Coating of Metal with Nano-Sized Hydroxyapatite.

Recent advances in multifunctional hydroxyapatite coating by electrochemical deposition

Improvement in Ca and P incorporation in the coating on Ti by gas-assisted electrical discharge coating

Preparation and characterization of hydroxyapatite coatings on Ti6Al4V alloy by a sol-gel method