Abstract:Molecular dynamics simulations were conducted to investigate the high-speed grinding process of monocrystalline silicon with a single diamond abrasive grain.By analyzing the morphological characteristics of chips,phase transformation and dislocation movement in subsurface,the influence of ginding speed on subsurface damage and integrity of ground surface were investigated combining the evolution of superficial area in workpiece.The simulation results show that the bump of material in the front of the abrasive grain increased at a higher grinding speed.When the grinding speed was more than 200 m/s,the increment of volume of the chip was not obvious.However,the average temperatures at the contact area increased substantially due to the squeezing and friction generated between the grain and workpiece.The interactions among the grinding temperature,grinding force and adhesion effect gave diversity for friction coefficient in a rule of "high to small".As a result of the lattice deformation,lattice reconstruction and amorphous phase transformation,the grinding force presented a critical fluctuation in the chip formation.For machining the silicon,a kind of brittle material,the damage layer in subsurface experienced a change of "thin to thick" with the grinding speed going up.When the grinding speed increased,the atom lattices beneath the grain had no enough time for the rearrangement,which resulted in less amorphous structure as well as a consequence of a thinner damage depth.While the grinding speed was over than 150 m/s,the dominant factor was the high temperature in the machining area,a thicker damage layer was induced on account of the dislocation nucleation and motion.

Influences of the Viscosity of Slurry on Monocrystalline Silicon Surface Damage Caused by Nanoparticle Impact

An Investigation on the Monocrystalline Silicon Surface Damage Caused by Slurry Erosion

Atomic scale deformation in the solid surface induced by nanoparticle impacts

Material removal mechanisms of monocrystalline silicon under the impact of high velocity micro-particles

Effect of Counter-Surface Chemistry on Defect-Free Material Removal of Monocrystalline Silicon

Theoretical Study on the Monocrystal Silicon Nanometric Grinding Process

Erosion Mechanisms of Monocrystalline Silicon under A Microparticle Laden Air Jet

Repulsion Mechanism of Nanoparticle Colliding with Monocrystalline Silicon Surface

Effects of grinding speeds on the subsurface damage of single crystal silicon based on molecular dynamics simulations

Interaction Mechanism Between Nanoparticles and Ultra-Smooth Surface under Effect of Cavitation

Atomistic Structural Change of Silicon Surface under A Nanoparticle Collision

Effect of Nanoparticle Impact on Material Removal

Phase Transformations of Monocrystalline Silicon Surface under Nanoparticle Collision

Study on Subsurface Damage of Wafer Silicon Containing Through Silicon Via in Thinning

Subsurface Damage in High-speed Grinding Process of Monocrystalline Silicon Based on Molecular Dynamics

Molecular Dynamics Analyze on Effects of Abrasive Size and Cut Depth on the Monocrystal Silicon Grinding

Material Removal Mechanism Of Nanoparticle Colloid Jet Polishing Based On Molecular Dynamics Simulation

Molecular Dynamics Simulation on Subsurface Damage Layer During Nano Grinding Process of Silicon Wafer

Effect of Roughness and Wettability of Silicon Wafer in Cavitation Erosion

Variations of a Ni-P Surface Layer after Nanoparticle Impacts

Subsurface Damage in the Monocrystal Silicon Grinding on Atomic Scale