Studies on selective oxidation of methane to methanol over Mo/La-Co-O catalyst
Xin Zhang,Dehua He,QiJian Zhang,Qing Ye,Boqing Xu,QiMing Zhu
IF: 16.5
2003-01-01
Chinese Journal of Catalysis
Abstract:The La-Co-O ( perovskite-type oxide), being selected as catalyst support for its high ability in activation Of 02, was prepared by sol-gel method using citric acid. A series of Mo/La-Co-O catalyst samples with different Mo-loading were prepared by wetness impregnation method. The catalytic performance of the catalyst samples in selective oxidation of CH4 to CH3OH was tested. The reaction resulted in products CH3OH, CO and CO2 over these catalyst samples. With the increase of Mo-loading, CH4 conversion gradually increased and CH3OH selectivity gave maximum value on 7% Mo/La-Co-O catalyst. The CH3OH selectivity of ca 60% and its yield of ca 6.7% were achieved under the conditions of n (CH4) : n (O-2): n (N-2) = 10 : 1 : 1, SV = 14.4 L/(g(.)h), p = 4.2 MPa and theta = 420 degreesC. And the CH3OH selectivity and yield continuously increased with the increase of reaction temperature on 7 % Mo/La-Co-O catalyst. The properties of the catalyst, such as structure, reducibility, oxidation state of surface ions, surface composition etc, were characterized by using BET, XRD, LRS, H-2-TPR and XPS techniques. The catalyst is mainly composed of LaCoO3 and Co3O4. The molybdena is amorphous and is well dispersed when it is loaded on La-Co-O. On the other hand, there exists interaction between the loaded Mo and the support La-Co-O, and thus modifies the properties of the catalyst. With the increase of Mo-loading, the reducibility of the catalyst is improved, and the O-/O2- ratio on the catalyst surface decreases. The reducibility and the O-/O2- ratio can determine the catalytic performance of Mo/La-Co-O catalyst in the selective oxidation of CH4 to CH3OH. The proper reducibility and proper O-/O2- ratio of the catalyst can enhance the selectivity and yield of CH3OH.