Abstract:Low sintering temperature ZnNb2O6 microwave ceramics were prepared by doping with mixed oxides of V2O5–Bi2O3 and V2O5–Bi2O3–CuO. The effects of additives on the microstructure and dielectric properties of the ceramics were investigated. The results show that doping with V2O5–Bi2O3 can reduce the sintering temperature of ZnNb2O6 from 1150°C to 1000°C due to the formation of V2O5 and Bi2O3 based eutectic phases. The combined influence of V2O5 and Bi2O3 resulted in rod-like grains. Co-doping CuO with 1wt.% V2O5–1wt.% Bi2O3 further lowered the sintering temperature to 880°C, because eutectic phases could be formed between the CuO, V2O5 and Bi2O3. A second phase of (Cu2Zn)Nb2O8 also forms when the content of CuO is greater than 2.5wt.%. A pure ZnNb2O6 phase can be obtained when the amount of CuO was 1.0–2.5wt.%. The Q×f values of ZnNb2O6 ceramics doped with V2O5–Bi2O3–CuO were all higher than 25,000GHz. The dielectric constants were 22.8–23.8 at microwave frequencies. In addition, theτf values decreased towards negative as the content of CuO increased. The ceramic with composition of ZnNb2O6+1wt.%V2O5+1wt.% Bi2O3+2.5wt.% CuO sintered at 880°C exhibited the optimum microwave dielectric properties, ɛ is 23.4, Q×f is 46,975GHz, and τf is −44.89ppm/°C, which makes it a promising material for low-temperature co-fired ceramics (LTCCs).

Low Temperature Sintering Microwave Dielectric Ceramic of ZnO-Nb2O5-TiO2 with FeVO4 Addition

Microwave Dielectric Properties of Low Temperature Sintered ZnWO4–TiO2 Composite Ceramics

Effect of ZnO-V2O5 Co-Doping on Phase Stability and Microwave Dielectric Properties of ZnTiO3 Ceramics

Effect of ZnO-V2O5Co-doping on phase stability and microwave dielectric properties of ZnTiO3 ceramics

Structure and Microwave Dielectric Properties of Low-Temperature Sintered ZnO-TiO2 Ceramics

Low-temperature firing and microwave dielectric properties of ZnO–Nb2O5–TiO2–SnO2 ceramics with CuO–V2O5

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Microstructure and Dielectric Properties of Low Temperature Sintered ZnNb2O6 Microwave Ceramics

Low Temperature Sintering of Li2Zn3Ti4O12–xTiO2 Microwave Dielectric Ceramics Without Glass Addition

Low-temperature Sintering and High-Frequency Dielectric Properties of ZTS Ceramics with V 2 O 5 –B 2 O 3 Addition

Effect of ZnO Ratio on Sintering Behavior and Microwave Dielectric Properties of BaO–ZnO–TiO2 Ceramics

Low-temperature Sintering and Microwave Dielectric Properties of ZnTiO3-based LTCC Materials

The phase transitions and dielectric properties of low temperature sintered ZnNb 2 O 6 –Zn 3 Nb 2 O 8 –TiTe 3 O 8 microwave ceramics

Low-fired microwave dielectrics in ZnO-TiO 2 ceramics doped with CuO and B 2 O 3

Research on Low Temperature Sintering of ZnO-TiO_2 Ceramics Doped with Li_2CO_3-B_2O_3-V_2O_5

Low-firing, Temperature Stable and Improved Microwave Dielectric Properties of ZnO TiO2Nb2O5 Composite Ceramics

Preparation and microwave dielectric properties of 3ZnO·B 2O 3 ceramics with low sintering temperature

EFFECT OF DOPING IN LOW-TEMPERATURE SINTERING OF Ca[(Li1/3Nb2/3)0.8Ti0.2]O3-σ MICROWAVE DIELECTRIC CERAMICS

Microwave Dielectric Properties of Cuo-V2o5-Bi2o3-Doped Znnb2o6 Ceramics with Low Sintering Temperature

Silver Co-Firable Zntinb2o8 Microwave Dielectric Ceramics With Li2o-Zno-B2o3 Glass Additive

Low Temperature Sintering and Microwave Dielectric Properties of Li 2 O–3ZnO–5TiO 2 Ceramics Doped with V 2 O 5