Preparation of fine-grains TiAl alloys by mechanical alloying and spark plasma sintering

Fantao Kong,Hongbao Yu,Yuyong Chen,Jiecai Han

2005-01-01

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

Abstract:Mechanical alloying and spark plasma sintering (SPS) technique were used to prepare the TiAl intermetallics. The mechanical alloying results show that the elemental powders mixture are transformed into nano powders after milled 15 h, and the particles sizes of that mixture are less than 100 nm. The mixture was then subjected to SPS at 800°C-1250°C in vacuum at 0.2 Pa for 6 min, and the sintering pressure was 30 MPa. X-ray diffraction (XRD) patterns showed that the sintered products mainly consisted of TiAl and Ti3Al phases. In addition, grain sizes of the sintered materials are increased with the rise of the sintering temperature, and the grain sizes can change from less than 200 nm to more than 1μm with the sintering temperature changing from 800°C to 1250°C. Vickers-hardness of the block materials after sintering at 950°C can reach 10 854 MPa.