Preparation of Ti-45Al-5.5(Cr,Nb,B,Ta) Alloy by Mechanical Milling and Spark Plasma Sintering
XIAO Shu-long,YU Hong-bao,HAN Jie-cai,XU Li-juan,CHEN Yu-yong
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2010.s1.068
2010-01-01
The Chinese Journal of Nonferrous Metals
Abstract:A fine-grained TiAl alloy with composition of Ti-45Al-5.5(Cr,Nb,B,Ta)(mole fraction,%) was prepared by double mechanical milling(DMM) and spark plasma sintering(SPS).The effects of sintering temperature on the microstructure and mechanical properties of the Ti-45Al-5.5(Cr,Nb,B,Ta) were studied by X-ray diffractometry(XRD), scanning electron microscopy(SEM) and mechanical testing machine.The results show that the morphology of double mechanical milling powder is regular with sizes of 10-40μm and the internal structure is even.TiAl and Ti_3Al are the main phases in the powders,with few phases such as Ti_3Al,Ti_2Al and TiB_2 observed in the SPS bulk samples of Ti-45Al-5.5(Cr,Nb,B,Ta) alloy.For samples sintered at 1 000℃,the microstructure of equiaxed crystal grain with sizes less than 500 nm is achieved.For samples sintered at 1 100℃,the sizes of few equiaxed crystal grain obviously increases.The SPS bulk samples exhibit better microstructures.The micro-hardness of the SPS bulk samples at 1 000℃is obviously lower than that of the SPS bulk samples at 1 100℃.The compression strength and bending strength of the SPS bulk samples at 1 000℃is obviously higher than that of the SPS bulk samples at 1 100℃.On the base of analysis of fractographies,it shows that the compression fracture transformation of the SPS Ti-45Al-5.5(Cr,Nb,B,Ta) alloy at 1 000℃is intergranular rupture and that at 1 100℃is intergranular rupture and cleavage fracture.The bending fracture transformation of the SPS Ti-45Al-5.5(Cr,Nb,B,Ta) alloy samples is intergranular rupture and cleavage fracture.