Preparation of TiAl-based alloys by mechanical milling and reactive sintering

Xiaoqiang Li,Lianxi Hu,ErDe Wang

2001-01-01

Abstract:The preparation of TiAl-based alloys by mechanical milling and reactive sintering has been studied. It is revealed that the Ti-Al composite powder with lamellar structure of alternative Ti and Al can be obtained from the elemental Ti and Al powder mixture by mechanical milling. With the increase of milling time, the lamellar structure of Ti-Al composite powder becomes thinner and more uniform. From the diffusion reaction performed at the solid state of the Ti-Al composite powder billet, it is found that mechanical milling can accelerate the diffusion reaction between Ti and Al, and that the Ti-Al composite powders can be completely transformed into TiAl compounds. Being sintered further at higher temperature, the TiAl-based alloys with near-full density are obtained from the reacted billet, and the typical microstructure of TiAl-based alloys with fine grains and lamella of small thickness are also obtained.